- Effect of Cr Addition on Tensile Properties of Ti-Fe-Cr beta Alloys Quenched From Beta Single Phase Region at 1173 K
- ベータソウ ヤキイレ Ti Fe Cr ベータ ゴウキン ノ ヒッパリ トクセイ ニ オヨボス Cr テンカ ノ エイキョウ
この論文をさがす
抄録
In beta quenched Ti-Fe-Cr alloys prepared using ferro-chromium alloy, pure Fe or pure Cr and as targeting composition to electron-to-atom ratio (e/a) of 4.28, phase constitution and tensile properties were investigated by electrical resistivity measurement, X-ray diffraction and tensile testing.<BR>In all alloys, beta phase was only identified by X-ray diffraction at room temperature. Resistivity and Vickers hardness decreased with increase in Cr content as a substitute for Fe on condition that 4.28 as e/a is maintained, whereas resistivity ratio increased with Cr content. These changes will be due to decrease in volume fraction of athermal omega with increase in Cr content.<BR>Tensile strength slightly decreased with increase in Cr content, whereas elongation and reduction in area obviously increased. The tensile properties of the quenched Ti-Fe-Cr alloys were not worse than those of commercial beta Ti alloys, excepting Ti-7.1Fe alloy. It is considered that addition of Cr as a substitute for Fe will improve balance between tensile strength and ductility.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 64 (5), 279-282, 2000
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681467826432
-
- NII論文ID
- 10005740407
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
- http://id.crossref.org/issn/00214876
- http://id.crossref.org/issn/00214426
-
- NDL書誌ID
- 5396380
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可