- Improvement of Mechanical Properties of 3004 Aluminum Alloy by Heavy Working at Cryogenic Temperature
- キョクテイオン アツエン ニ ヨリ キョウ カコウ シタ 3004Al ゴウキン ノ キカイテキ トクセイ ノ コウジョウ
この論文をさがす
抄録
To improve the mechanical properties of Al alloys, grain refinement is one of the useful methods. In this study, grain refinement of 3004Al alloy was carried out by heavy plastic working i.e. warm or cryogenic forging, which induced high stored strain energy. It was possible to be rolled up to 98% reduction ratio by using cryogenic rolling with forging as prework process. Annealing was finally performed for rapid recrystallization in a salt bath at recrystallization temperature. As the result, Vickers hardness, tensile strength and yield stress of specimens worked up to 98% were HV160, 450 and 390 MPa, respectively. The specimens having annealing treatment at 583 K, 300 s produced fine grain structures with about 5 mm in grain size. It was found that the yield stress and tensile strength were 1.6 and 1.2 times compared with that of initial material regardless of forging condition. In the case of shorter annealing time, i.e. 30 s, the grain size was 3∼4 μm and yield stress increment of 2.5 times was obtained. This working process is more practical and easy to enhance its mechanical properties.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 64 (5), 395-399, 2000
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681467789568
-
- NII論文ID
- 130007341675
- 10005740726
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 5396808
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可