Alignment of Ferrite Grains during Austenite to Ferrite Transformation in a High Magnetic Field
-
- Ohtsuka Hideyuki
- Tsukuba Magnet Lab., National Research Institute for Metals
-
- Xu Ya
- Tsukuba Magnet Lab., National Research Institute for Metals
-
- Wada Hitoshi
- Tsukuba Magnet Lab., National Research Institute for Metals
この論文をさがす
抄録
Effects of a high magnetic field on austenite to ferrite transformation behavior were investigated in Nb containing steel. It was found that the isothermal ferrite transformation was accelerated by applying a magnetic field, mainly due to an increase in the nucleation rate of ferrite and no fundamental change in the transformed structure was observed. Recently, Shimotomai et al. showed that an aligned, two-phase structure is obtained by a reverse-transformation from lath martensite in a magnetic field. Considering the conditions of this heat treatment, it is expected that the aligned structure can also be formed in austenite to ferrite transformation. In this paper, the alignment of ferrite grains during austenite to ferrite transformation in a high magnetic field is reported.
収録刊行物
-
- Materials Transactions, JIM
-
Materials Transactions, JIM 41 (8), 907-910, 2000
社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204247584256
-
- NII論文ID
- 130003557417
- 10005746371
-
- NII書誌ID
- AA10699969
-
- COI
- 1:CAS:528:DC%2BD3cXnt12hur0%3D
-
- ISSN
- 2432471X
- 09161821
- http://id.crossref.org/issn/00214434
- http://id.crossref.org/issn/09161821
-
- NDL書誌ID
- 5505623
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可