Effect of Graphite Morphology on Tensile Properties of Flake Graphite Cast Iron
-
- Nakae Hideo
- Department of Materials Science and Engineering, Waseda University
-
- Shin Hochul
- Department of Materials Science and Engineering, Waseda University
この論文をさがす
抄録
The mechanical properties of flake graphite cast iron were studied using normal cast and unidirectionally solidified (UDS) test pieces. Their chemical composition was eutectic, namely CE=4.3%, differing only in sulfur content. To eliminate the influence of the discontinuity of graphite at the eutectic cell boundary, we used UDS samples. Fully annealed tensile test pieces were used to exclude the influence of the matrix. The experimental results are as follows: The tensile strength and elongation of normal and unidirectionally solidified cast iron are increased by the sulfur addition as the graphite morphology is modified. The tensile strength is improved by UDS . One of the reasons must be based on the continuity of the matrix. Nevertheless, the tensile strength of the UDS samples is not as strong as that of spheroidal graphite cast iron because the fracture occurs at the graphite-terminated area in the aligned graphite samples.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 42 (7), 1428-1434, 2001
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204248435200
-
- NII論文ID
- 130004451587
- 10006551181
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD3MXmsFyrtr0%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 5889840
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可