- Relationship between the Crystallographic Structure of Electrodeposited Ni-W Alloy Film and Its Thermal Equilibrium Diagram
- デンセキNi W ゴウキンメッキ マク ノ ビサイ コウゾウ ト ネツ ヘイコウ ジョウタイズ ト ノ カンケイ
この論文をさがす
抄録
Electrodeposited Ni-W alloy films were obtained from Nickel Sulfate baths containing Na2WO4. The crystallographic structure and morphology of electrodeposited Ni-W films were studied by XRD, HRTEM, SEM and heat-treatment technique. The crystallographic structures of electrodeposited Ni-W alloy films were also compared with the Ni-W thermal equilibrium diagram.<BR>The X-ray diffraction patterns of Ni-W electrodeposited films with various W contents gradually changed from sharp peaks to broad peaks with increasing W contents in electrodeposited films. HRTEM observation revealed that the crystallographic structure of electrodeposited Ni-W film with 19.7 at%W content was crystalline and its crystal size was about 10 nm. Moreover, the crystalline structure was observed and the crystal size was about 5 nm in the electrodeposited Ni-W alloy film with 24.4 at%W content. However, when the film with 24.4 at%W content was heat treated, the crystalline phase did not grow and an unknown phase (Ni4W?) existed alone under 600°C heat-treatment. From this result, it was clear that the crystallographic structure of Ni-W film with 24.4 at%W content was amorphous.<BR>Therefore, it can be concluded that the microcrystalline phase existed up to 22 at%W in electrodeposited Ni-W alloy film and the amorphous phase existed from 22 at% to 35 at%W.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 65 (11), 1023-1028, 2001
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681468238592
-
- NII論文ID
- 130007342136
- 10007481389
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 5990277
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可