温間圧延による7475系アルミニウム合金板材の結晶粒微細化

• 箕田 正

  住友軽金属工業（株）研究開発センター

• 田中 宏樹

  住友軽金属工業（株）研究開発センター

• 渋江 和久

  住友軽金属工業（株）研究開発センター

• 吉田 英雄

  住友軽金属工業（株）研究開発センター

書誌事項

タイトル別名

• Grain refinement of 7475 based aluminum alloy sheet by warm rolling
• オン カン アツエン ニ ヨル 7475ケイ アルミニウム ゴウキン イタザイ ノ ケッショウリュウ ビサイカ

抄録

The effect of transition element on grain refinement of 7475 aluminum alloy sheet produced by warm rolling was investigated. The alloy which contains zirconium instead of chromium showed ultra fine structure with stable subgrain structure after warm rolling at 350°C, followed by solution heat treatment at 480°C. The average size of subgrains was about 2 μm in diameter. Furthermore, it became clear that zirconium in solution has the effect of stabilizing subgrains. That is, fine Al₃Zr compounds precipitate during warm rolling, inhibit recrystallization and stabilize subgrains. While, in the case of the 7475 alloy with only chromium, recrystallization occurs during warm rolling, because chromium-bearing compounds precipitate in relatively large size and they have less effect of inhibiting recrystallization. Moreover, the alloy containing both chromium and zirconium showed a duplex structure with recrystallized grains and subgrains.

収録刊行物

• 軽金属

  軽金属 51 (12), 651-655, 2001

  一般社団法人 軽金属学会

キーワード

• super metal
• warm rolling
• Al–Zn–Mg
• grain refinement
• transition element

詳細情報

• CRID: 1390001206338177024
• NII論文ID: 10007482628
• NII論文ID: 10008559354
• NII書誌ID: AN00069773
• DOI: 10.2464/jilm.51.651
• COI: 1:CAS:528:DC%2BD38XhslGjt74%3D
• ISSN: 18808018
• ISSN: 04515994
• NDL書誌ID: 6018341
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I6018341
• Web Site: https://www.jstage.jst.go.jp/article/jilm/51/12/51_12_651/_pdf
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可