Desulfurization Ability of Metallurgical Dusts from Blast Furnace Ironmaking Process.
-
- SHUFENG YE
- Institute of Chemical Metallurgy, Chinese Academy of Sciences
-
- YUSHENG XIE
- Institute of Chemical Metallurgy, Chinese Academy of Sciences
-
- ZHANCHENG GUO
- Institute of Chemical Metallurgy, Chinese Academy of Sciences
-
- XUEMIN YANG
- Institute of Chemical Metallurgy, Chinese Academy of Sciences
-
- YUNFA CHEN
- Institute of Chemical Metallurgy, Chinese Academy of Sciences
この論文をさがす
抄録
The sulfur capacity of metallurgical dusts from blast furnace ironmaking processes was measured in the temperature range from 298 to 923 K. The experimental results show that the sulfur capacity of metallurgical dusts is considerably increased with the increase of temperature from 298 to 923 K. The desulfurization ability of metallurgical dusts is mainly depend on its content of oxides of ZnO, PbO, CaO and MnO when the temperature is lower than 623 K, but when the temperature is higher than 623 K the contributions of iron oxides become dominant. Carbon content, due to its absorption effect, has a positive effect on the desulfurization ability of metallurgical dusts below 623 K. If the temperature increased to higher than 623 K the absorption effect of carbon disappears and the role of desulfurization reaction between H2S and the metal oxide such as ZnO, PbO, Fe2O3, CaO and MnO as well as the H2S diffusion in intraparticle of metallurgical dusts seems more important.
収録刊行物
-
- JOURNAL OF CHEMICAL ENGINEERING OF JAPAN
-
JOURNAL OF CHEMICAL ENGINEERING OF JAPAN 34 (9), 1103-1107, 2001
公益社団法人 化学工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679543835904
-
- NII論文ID
- 10007564492
-
- NII書誌ID
- AA00709658
-
- COI
- 1:CAS:528:DC%2BD3MXnt1Cktb4%3D
-
- ISSN
- 18811299
- 00219592
-
- NDL書誌ID
- 5991803
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可