熱サイクル負荷が前装用硬質レジンの表面性状に与える影響 Influence of Thermal Cycle Stress on Surface Texture of Prosthetic Composite Resin

この論文にアクセスする

この論文をさがす

著者

    • 村口 浩一 MURAGUCHI Kouichi
    • 鹿児島大学歯学部歯科補綴学第一講座 The 1 St Department of Prosthetic Dentistry, Kagoshima University, Dental School
    • 南 弘之 MINAMI Hiroyuki
    • 鹿児島大学歯学部歯科補綴学第一講座 The 1 St Department of Prosthetic Dentistry, Kagoshima University, Dental School
    • 木村 孝広 KIMURA Takahiro
    • 鹿児島大学歯学部歯科補綴学第一講座 The 1 St Department of Prosthetic Dentistry, Kagoshima University, Dental School
    • 嶺崎 良人 MINESAKI Yoshito
    • 鹿児島大学歯学部歯科補綴学第一講座 The 1 St Department of Prosthetic Dentistry, Kagoshima University, Dental School
    • 鬼塚 雅 ONIZUKA Tadashi
    • 鹿児島大学歯学部歯科補綴学第一講座 The 1 St Department of Prosthetic Dentistry, Kagoshima University, Dental School
    • 田中 卓男 TANAKA Takuo
    • 鹿児島大学歯学部歯科補綴学第一講座 The 1 St Department of Prosthetic Dentistry, Kagoshima University, Dental School

抄録

目的: 硬質レジン前装冠は, 審美的修復物として臨床においてしばしば用いられている. 接着技法の進歩により, 前装部レジンが金属フレームから脱落することを経験する機会は減少している. しかし, それに伴い, 装着後長期間経過すると, 変色や光沢の消失など前装部レジンの劣化が認められ, 審美性の低下が引き起こされる. 熱サイクル負荷は, 前装用硬質レジンの劣化を引き起こす原因の1つと考えられるが, その影響は解明されていない. 本研究では, 熱サイクル負荷が, 前装用硬質レジンの表面性状に与える影響について検討を行った.<BR>方法: 4種類の光重合型の前装材料を用いて, 正方形 (8×8×1.5mm) の試験片を作製し, 測定面は臨床での技法に準じて研磨した. 4°Cと60°Cの水中に60秒ずつ浸漬する熱サイクル負荷を最大で50, 000回付与した後に, 肉眼的観察や色素浸透試験, 表面粗さの測定, 走査型電子顕微鏡 (SEM) による微細構造の観察を行った.<BR>結果: 熱サイクル負荷後の試験片では, 肉眼的には粗造感と光沢の消失が認められ, 色素浸透試験による色素の浸透は増大した. また, 表面粗さは負荷前に比較して増加した. さらに, SEM観察では, クラックや陥凹の発生が認められた.<BR>結論: これらのことから, 熱サイクル負荷は, 硬質レジンの表面性状に多くの変化を引き起こし, 審美性を低下させる要因であることが明らかとなった.

Purpose: Resin facing crowns are frequently used clinically as aesthetic restorations. Improvement of the adhesion between prosthetic composite resin and the dental alloy decreased the debonding of the resin from the metal frame. However, shade or luster of the resin surface change gradually over a long time, resulting in poor appearance. Although it is easily expected that thermo-cycle testing should affect the surface texture of prosthetic composite resin, details have never been clarified. The purpose of this investigatixon was to clarify the effects of thermo-cycle testing on surface texture of prosthetic composite resin.<BR>Methods: Square (8×8×1.5mm) specimens were fabricated by 4 photo-curing prosthetic composite resin. The measuring surface was polished according to the clinical procedure. Surface textures before and after thermo-cycle testing (4°C60°C) were investigated by macroscopic observation, pigment penetration test, measurement of surface roughness and scanning electron microscopic (SEM) observation of the microstructure.<BR>Results: Macroscopic observation revealed a rough mat surface, and the pigment penetrations were increased on the thermo-cycled specimens. Surface roughness of the thermo-cycled specimens was increased as compared with that of the non-thermo-cycled specimens. Furthermore, SEM observation demonstrated cracking and partial peeling of the thermo-cycled resin surface.<BR>Conclusions: Since thermo-cycle stress causes various changes to the surface texture of the prosthetic composite resin, it is an important factor, which deteriorates the aesthetic quality.

収録刊行物

  • 日本補綴歯科學會雜誌 = The journal of the Japan Prosthodontic Society

    日本補綴歯科學會雜誌 = The journal of the Japan Prosthodontic Society 46(2), 251-259, 2002-04-10

    Japan Prosthodontic Society

参考文献:  25件中 1-25件 を表示

被引用文献:  1件中 1-1件 を表示

各種コード

  • NII論文ID(NAID)
    10008157073
  • NII書誌ID(NCID)
    AN00197911
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    03895386
  • データ提供元
    CJP書誌  CJP引用  J-STAGE 
ページトップへ