陶材前装コーヌスクローネ用合金に関する研究 : 第1報 多目的用金合金の焼付強度 Study on Porcelain-Fused Alloy for Conical Double-Crown Telescopics Prosthesis : Part 1 Bond Strength of Multi-Purpose Gold Alloy

この論文にアクセスする

この論文をさがす

著者

    • 清野 豊 KIYONO Yutaka
    • 昭和大学歯学部第三歯科補綴学教室 The Third Department of Prosthodontics, Showa University School of Dentistry
    • 芝 あき彦 SHIBA Akihiko
    • 昭和大学歯学部第三歯科補綴学教室 The Third Department of Prosthodontics, Showa University School of Dentistry

抄録

Multi-purpose gold alloys (Degunorm, Degudent LTG) were investigated as casting metal for conical double-crown telescopic prosthesis. Bond strength between porcelain and metal was compared to conventional ceramo-metal system. In addition, bond strength with some four treatments was also examined. The results were as follows:<BR>1. Bond strength of multi-purpose gold alloy with its original low-fused porcelain was similar to those of conventional dental porcelain-fused metal.<BR>2. Bond strength of Degunorm painted bonding agent after sandblasting showed the highest value under all test conditions in this study.<BR>3. According to SEM observation, body-opaque interface after firing was definite. However, bondingopaque interface was not distinguishable.<BR>4. The values of Vickers hardness (Hv) for body, opaque and bonding porcelain were 712, 325 and 468respectively.<BR>5. Particle size of opaque porcelain was approximately 50 pm, and was coarser than that of bonding porcelain.<BR>6. Leucite was detected in all of porcelain powders before firing. However, the leucite peak of body powder drawn in the X-ray diffraction chart was not obviously steep because it was amorphous.

収録刊行物

  • 日本補綴歯科學會雜誌 = The journal of the Japan Prosthodontic Society

    日本補綴歯科學會雜誌 = The journal of the Japan Prosthodontic Society 43(5), 781-790, 1999-10-10

    Japan Prosthodontic Society

参考文献:  33件中 1-33件 を表示

被引用文献:  1件中 1-1件 を表示

各種コード

  • NII論文ID(NAID)
    10008174299
  • NII書誌ID(NCID)
    AN00197911
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    03895386
  • データ提供元
    CJP書誌  CJP引用  J-STAGE 
ページトップへ