乾式カップリング処理に用いるVTESおよびVTMS溶液のオリゴマー生成 Formation of Oligomers of VTES and VTMS

この論文にアクセスする

この論文をさがす

著者

抄録

Since the oligomer state of the coupling agent plays an important role in the hydrophobicity of inorganic oxides, various factors affecting the time variation in the average polymerization degree, determined through GPC analysis of preliminary treatment solution and water content determined by the Carl-Fisher method, were studied for the VTES or VTMS-Alcohol-H<sub>2</sub>O system. The main findings obtained are as follows: (1) The existence of a close relationship between the decreasing rate of the coupling agent monomer and time variation of the height of GPC elution peaks for polymer was qualitatively detected. (2) Time variation of polymerization degree determined from water content of the preliminary treatment solution is intimately related to the progressive rate of oligomer formation reaction. (3) Decreasing rates of water concentration in the preliminary treatment solution were increased by the increase in the initial water concentration, decrease in the alcohol concentration as well as the pH value of the aqueous solution and the elevation of temperature and lowered by the sequence MeOH, EtOH and <i>i</i>-PrOH.

収録刊行物

  • 表面技術 = The Journal of the Surface Finishing Society of Japan

    表面技術 = The Journal of the Surface Finishing Society of Japan 53(6), 393-399, 2002-06-01

    The Surface Finishing Society of Japan

参考文献:  8件中 1-8件 を表示

  • <no title>

    吉岡博

    表面 21(3), 157, 1983

    被引用文献9件

  • <no title>

    富永健治

    ポリマーダイジェスト 34(3), 23, 1982

    被引用文献3件

  • <no title>

    永江利康

    顔料 26(2), 1595, 1985

    被引用文献4件

  • <no title>

    佐貫須美子

    表面技術 50, 84, 1999

    被引用文献4件

  • <no title>

    佐貫須美子

    表面技術 51, 828, 2000

    被引用文献5件

  • <no title>

    POHL E. R.

    Controlled interface in Composite Materials, 37-50, 1990

    被引用文献2件

  • <no title>

    PLUEDDEMANN E. P.

    Silane coupling agents, 55-78

    被引用文献1件

  • <no title>

    藤田直克

    松下電工技報 50, 14, 1995

    被引用文献3件

各種コード

  • NII論文ID(NAID)
    10008556772
  • NII書誌ID(NCID)
    AN1005202X
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    09151869
  • NDL 記事登録ID
    6185240
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-291
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ