Effect of Niobium on Nitrogen Solubility in High Chromium Steel.
-
- Lee Sang-Beom
- Pohang University of Science and Technology
-
- Jung Myung-Chae
- POSCO
-
- Song Hyoseok
- POSCO
-
- Rhee Chang-Hee
- Pohang University of Science and Technology
Search this article
Abstract
The interaction parameters of alloying elements on nitrogen in liquid Fe-Cr alloys containing niobium have been determined. The equilibrium nitrogen solubility in the liquid iron alloy was measured by metal-gas equilibrium technique under 0.04 to 1.0 atm of nitrogen atmosphere at 1 823 to 1 923K. Nitrogen solubility in Fe-Cr-Nb melts obeyed Sieverts' law for all compositions studied in present study.<br>The results obtained are summarized as follows;<br>(1) The solubility of nitrogen markedly increased with increasing chromium and niobium. The interactionparameters in liquid iron alloys containing 10-18 % of Cr and 0.2-2 % of Nb are obtained.<br>(2) The solubility of nitrogen was lower at a higher temperature in Fe-Cr melts in this study.<br>(3) Test results indicated that it is not likely to form niobium nitride in Fe-Cr-Nb-N alloys and it was confirmed by EDS.
Journal
-
- ISIJ International
-
ISIJ International 42 (6), 603-608, 2002
The Iron and Steel Institute of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390001206453135232
-
- NII Article ID
- 10008563947
-
- NII Book ID
- AA10680712
-
- COI
- 1:CAS:528:DC%2BD38XlslKht7o%3D
-
- ISSN
- 13475460
- 09151559
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed