臨床例における磁性アタッチメント用キーパーと歯科鋳造用合金との鋳接状態 Conditions of Casting Au-Ag-Pd Alloy to an Embedded Keeper of Magnetic Attachment in Clinical Cases

この論文にアクセスする

この論文をさがす

著者

    • 浅野 彰夫 ASANO Akio
    • 朝日大学歯学部歯学科補綴学講座 Department of Prosthodonitcs, Asahi University School of Dentistry
    • 山内 六男 YAMAUCHI Mutsuo
    • 朝日大学歯科臨床研究所附属歯科診療所 Dental Clinic, Post-doctoral Institute of Clinical Dentistry, Asahi University
    • 堺 誠 SAKAI Makoto
    • 朝日大学歯学部歯学科補綴学講座 Department of Prosthodonitcs, Asahi University School of Dentistry
    • 岸井 次郎 KISHII Jiro
    • 朝日大学歯学部歯学科補綴学講座 Department of Prosthodonitcs, Asahi University School of Dentistry
    • 長澤 亨 NAGASAWA Tooru
    • 朝日大学歯学部歯学科補綴学講座 Department of Prosthodonitcs, Asahi University School of Dentistry

抄録

目的: われわれは先にキーパーと12%金銀パラジウム合金の鋳接状態について基礎的に検討し, 接合部には酸素を固溶した反応層と間隙 (黒色層) がわずかながら存在し, これは鋳型の係留温度や鋳造方法などによって影響を受けることを報告した.本報告では, 実際に口腔内に装着されたキーパー付き根面板における鋳接状態について検討した.<BR>方法: 被験歯数は7歯で, すべて歯周疾患によって抜去されたものである.鋳造用合金にはすべて12%金銀パラジウム合金が使用されていた.鋳造はすべて遠心鋳造機により行われていた.根面板を支台歯とともにレジンにて包埋し中央にて割断後, 金属顕微鏡および走査型電子顕微鏡にてキーパーと鋳造用合金との接合部を観察した.また, X線電子マイクロアナライザーによる分析を行った. これらを既報告で良好な鋳接状態が得られた条件における結果と比較した.<BR>結果: 金属顕微鏡観察からキーパーと鋳造用合金との接合部には黒色層が観察された. 黒色層は, 走査型電子顕微鏡およびX線電子マイクロアナライザー分析から, 間隙と反応層から構成されていた. この黒色層は基礎実験の結果に比べて厚く, 不均一であった.<BR>結論: キーパーの根面板への鋳接に際しては適切な鋳造条件を厳守する必要がある.

Purpose: We previously reported that an oxidation layer and space (black layer) were observed between the keeper and 12% Au-Ag-Pd alloy in a basic study. The black layer was affected by the mold temperature and casting method. In this report, conditions of casting dental alloys to an embedded keeper of magnetic attachment in clinical cases were investigated.<BR>Methods: Seven extracted teeth were investigated. These teeth were extracted due to periodontal disease. A 12% Au-Ag-Pd alloy was used as a casting alloy. Coping was cast by a centrifugationtype casting machine. The interface between the keeper and casting alloy was observed by light microscopy and scanning electron microscopy. Additionally, this interface was analyzed with an Xray electron microprobe. These resulting data were compared with those of a previous report.<BR>Results: By microscopic observation, the black layer was observed between the keeper and casting alloy in all specimens. By scanning electron microscopy and X-ray electron microprobe analysis, the black layer was composed of an oxidation layer and a casing defect. These black layers were larger than those of the bench test, and they had irregular thicknesses.<BR>Conclusions: The proper casting conditions are needed for casting Au-Ag-Pd alloy to an embedded keeper of magnetic attachment.

収録刊行物

  • 日本補綴歯科學會雜誌 = The journal of the Japan Prosthodontic Society

    日本補綴歯科學會雜誌 = The journal of the Japan Prosthodontic Society 46(3), 377-384, 2002-06-10

    Japan Prosthodontic Society

参考文献:  14件中 1-14件 を表示

被引用文献:  1件中 1-1件 を表示

各種コード

  • NII論文ID(NAID)
    10008630803
  • NII書誌ID(NCID)
    AN00197911
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    03895386
  • データ提供元
    CJP書誌  CJP引用  J-STAGE 
ページトップへ