- Effect of Thermo-mechanical Treatment on Ductile-Brittle Transition Behavior of Chromium
- クロム ノ エンセイ ゼイセイ センイ キョドウ ニ オヨボス カコウ ネツ ショリ ノ エイキョウ
この論文をさがす
抄録
High purity chromium powders were sintered into a block by means of hot isostatic pressing. Pieces taken from the sintered block were thermo-mechanically treated, i.e., repeatedly rolled at 973 K up to 50 and 85% in total reduction with and without intermediate annealing at 1273 K. The ductile-brittle transition temperature, DBTT, was determined by a tension test with the specimens cut from the as-sintered block and the rolled sheets. DBTT for the specimen rolled without intermediate annealing was about 600 K, while DBTT of the specimen rolled with the annealing was 400 K much lower than the above temperature 600 K and the temperature 500 K which was found in the as-sintered material. The reduction in DBTT through the thermo-mechanical treatment probably comes from the decrease of susceptibility to the occurrence of brittle fracture at grain boundaries.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 66 (5), 485-491, 2002
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681468777728
-
- NII論文ID
- 10008833112
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 6179017
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可