- Effect of second phase particles on the bendability of an Al-Mg-Si alloy.
- Al-Mg-Si系合金の曲げ加工性に及ぼす第2相粒子の影響
- Al Mg Siケイ ゴウキン ノ マゲ カコウセイ ニ オヨボス ダイ2ソウ リュウシ ノ エイキョウ
この論文をさがす
抄録
The effect of second phase particles on the bendability of Al–Mg–Si alloy for outer panels in autobodies was investigated by changing solution heat treatment condition and quenching rate. Slow quenching rate made inferior bendability. Because the number of second phase particles on the grain boundaries increased. Crack by bending test was not observed with short solution heat treatment time. However, in the case of long solution heat treatment time, the crack was observed. Depth of the crack increased with solution heat treatment time to maximum value and then decreased. The number of second phase particles decreased and the formation of shear bands by deformation increased with solution heat treatment time. When the formation of shear bands is observed significantly and the number of second phase particles is many, the crack occurs easily along the shear bands and the second phase particles.
収録刊行物
-
- 軽金属
-
軽金属 52 (10), 448-452, 2002
一般社団法人 軽金属学会
- Tweet
詳細情報
-
- CRID
- 1390282681312310656
-
- NII論文ID
- 10016764194
- 10010013576
- 10012537239
- 10015675775
-
- NII書誌ID
- AN00069773
-
- COI
- 1:CAS:528:DC%2BD3sXhs1Wgug%3D%3D
-
- ISSN
- 18808018
- 04515994
- http://id.crossref.org/issn/04515994
-
- NDL書誌ID
- 6339129
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可