Characteristics of Paramagnetic and Diamagnetic Anisotropy which Induce Magnetic Alignment of Micron-Sized Non-Ferromagnetic Particles
-
- Uyeda Chiaki
- Institute of Earth and Space Science, Graduate School of Science, Osaka University
-
- Tanaka Kenta
- Institute of Earth and Space Science, Graduate School of Science, Osaka University
-
- Takashima Ryouichi
- Institute of Earth and Space Science, Graduate School of Science, Osaka University
-
- Sakakibara Makoto
- Institute of Earth and Space Science, Graduate School of Science, Osaka University
この論文をさがす
抄録
The effect of temperature is discussed on the magnetic-alignment process of micron-sized particles dispersed in a fluid medium, based on the experimental data compiled on various non-ferromagnetic materials having different concentrations of paramagnetic impurity ion. The field-intensity required to achieve alignment decreased with temperature following the relation calculated from the Langevin theory, when the diamagnetic particles were free of paramagnetic ions. The rotational Brownian motion was considered to randomize the direction of the micro-crystals in the theory. The above-mentioned temperature dependence was expected to occur for most of the diamagnetic oxides, since the oxides were expected to posses a finite amount of diamagnetic anisotropy according to a model proposed recently to explain the origin of anisotropy. The decease of temperature caused additional reduction on the field-intensity to achieve alignment, when finite amount of paramagnetic ion was contained in the particle. This was because the paramagnetic anisotropy increased which the reduction of temperature. The doping of paramagnetic ion on non-ferromagnetic materials in the course of processing a material expected to reduce the field intensity to achieve magnetic alignment at room temperature. The above findings, concerned with the reduction of field intensity to achieve magnetic alignment, may increase the possibility of practical applications of the phenomena of magnetic alignment.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 44 (12), 2594-2598, 2003
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204250773760
-
- NII論文ID
- 130004452009
- 10011817874
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD2cXosVaqtg%3D%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 6796620
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可