This paper presents the tensile properties of cast and extruded Mg–8Al–xRE (in mass%; x is 0, 1, 2 or 3%) alloys from 300 to 673 K obtained at a strain rate of 8.3×10−4 s−1. Mg–8Al–xRE alloys were prepared by melting and casting in a vacuum induction furnace, and extruded at 633 K with a reduction ratio of 90:1. RE greatly improves the tensile strength of cast and extruded Mg8Al alloys above 473 K. RE negatively affects the elongation of cast alloys at the studied temperature range but considerably enhances that of extruded alloys. Superplasticity of the extruded alloys is observed at 473 K or above. The strengthening mechanisms and the optimal deformation temperature, Tc, of these alloys are discussed in detail.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 44 (5), 1029-1035, 2003
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204245879808
-
- NII論文ID
- 130004452131
- 10011912123
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD3sXlsVSjt7k%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 6537445
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可