Surface Tension and Wettability of Liquid Fe-16 mass%Cr-S Alloy with Alumina
-
- Li Zushu
- Department of Materials Science and Engineering, Faculty of Engineering, Kyushu Institute of Technology
-
- Zeze Masafumi
- Yawata R&D Lab, Technical Development Bureau, Nippon Steel Corporation
-
- Mukai Kusuhiro
- Department of Materials Science and Engineering, Faculty of Engineering, Kyushu Institute of Technology
書誌事項
- タイトル別名
-
- Surface Tension and Wettability of Liquid Fe 16 massパーセントCr S Alloy with Alumina
この論文をさがす
抄録
The surface tension and wettability of liquid Fe-16 mass%Cr-S alloy with alumina substrate at 1823 K and the temperature dependence of surface tension of liquid Fe-16 mass% Cr-S alloy in the temperature range of 1808-1883 K were measured using the sessile drop technique. The surface tension and contact angle of liquid Fe-16 mass%Cr-S alloys with alumina substrate decreased markedly with increasing sulphur concentration in the alloys. The variation of surface tension of liquid Fe-16 mass% Cr-S alloys with sulphur activity can be described by the following equation: σ1g=1640−182ln(1+157aS) (mass% O=0.0037-0.0075, mass% S ≤ 0.195) (mN/m). The interfacial tension between liquid Fe-16 mass% Cr-S alloys and alumina substrate, calculated using Young’s equation, can be expressed by the following equation: σs1=2170−220ln(1+237aS) (mass% O=0.0037-0.0075, mass% S ≤ 0.195) (mN/m). The work of adhesion between liquid Fe-16 mass% Cr-S alloys and alumina had a tendency to increase with increasing sulphur concentration. The temperature coefficient of surface tension, dσ⁄dT, for Fe-16 mass% Cr-S system in the temperature range of 1808-1883 K increased with increasing sulphur concentration, and changed from negative to positive value when the sulphur concentration exceeded 20 mass ppm.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 44 (10), 2108-2113, 2003
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679225047424
-
- NII論文ID
- 10011915987
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD3sXptFOns7k%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 6722273
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可