Effect of Morphology and Si Content on SiO2 Particle Erosion of Full Pearlitic Spheroidal Graphite Cast Iron
-
- Hung Fei-Yi
- Department of Materials Science and Engineering, National Cheng-Kung University
-
- Chen Li-Hui
- Department of Materials Science and Engineering, National Cheng-Kung University
-
- Lui Truan-Sheng
- Department of Materials Science and Engineering, National Cheng-Kung University
書誌事項
- タイトル別名
-
- Effect of Morphology and Si Content on SiO<SUB>2</SUB> Particle Erosion of Full Pearlitic Spheroidal Graphite Cast Iron
この論文をさがす
抄録
The effect of morphology and Si content on SiO2 particle erosion wear of full pearlitic spheroidal graphite cast iron was studied. Experimental data shows the specimens posses more area fraction of cementite for an identical silicon content, that contribute to improve erosion resistance. However, the specimens posses larger interlamellar spacing (λ) at increased Si content, even if the matrix hardness is higher that still debase the erosion resistance. The 2.1Si-air(930°C) specimens not only possess finer λ value and larger cementite fraction but also with better ductility, which could improve erosion resistance.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 43 (1), 42-48, 2002
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679222789888
-
- NII論文ID
- 130004451646
- 10012320398
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD38XitlSrtLY%3D
-
- ISSN
- 13475320
- 13459678
- http://id.crossref.org/issn/09161821
-
- NDL書誌ID
- 6051274
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可