Fabrication of Bulk Glassy Hf50Cu30Ni10Al10 Alloy by Copper Mold Casting
-
- Ma Liqun
- Institute for Materials Research, Tohoku University
-
- Wang Limin
- Inoue Superliquid glass Project, ERATO, JST
-
- Zhang Tao
- Institute for Materials Research, Tohoku University
-
- Inoue Akihisa
- Institute for Materials Research, Tohoku University
書誌事項
- タイトル別名
-
- Fabrication of Bulk Glassy Hf<SUB>50</SUB>Cu<SUB>30</SUB>Ni<SUB>10</SUB>Al<SUB>10</SUB> Alloy by Copper Mold Casting
この論文をさがす
抄録
The glass-forming ability of the Hf50Cu30Ni10Al10 alloy was examined by melt-spinning and copper mold casting methods. A new Hf50Cu30Ni10Al10 bulk glassy rod of 3 mm in diameter was formed by copper mold casting. The crystallization temperature (Tx), glass transition temperature (Tg) and Tg⁄Tl of the glassy alloy rod were 780 K, 860 K and 0.61, respectively. The Hf50Cu30Ni10Al10 bulk glassy alloy exhibits density of 11.0×103 kg/m3, Vickers hardness of 590, Young’s modulus of 118 GPa and compressive fracture strength of 2420 MPa. The synthesis of the Hf-based bulk glassy alloy with high Tg⁄Tl, high fracture strength and high density is encouraging for future application of bulk glassy alloys.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 43 (9), 2357-2359, 2002
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204247724544
-
- NII論文ID
- 10012326576
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD38XnvFGqtrY%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 6313566
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可