Synthesis of New Hydrides in Mg-Y Systems by Using High Pressure
-
- Goto Yasuyuki
- Department of Materials Science, Graduate School of Engineering, Tohoku University
-
- Kamegawa Atsunori
- Department of Materials Science, Graduate School of Engineering, Tohoku University
-
- Takamura Hitoshi
- Department of Materials Science, Graduate School of Engineering, Tohoku University
-
- Okada Masuo
- Department of Materials Science, Graduate School of Engineering, Tohoku University
この論文をさがす
抄録
A new hydride in the MgH2–YH3 system was found by using a high pressure of 5 GPa, and their crystal structure, thermal stability and hydrogen content were studied. The high-pressure synthesis was carried out at 1073 K for 2 h under 5 GPa by using an anvil-type apparatus. In the MgH2–xat%YH3 system (x=33–100), novel hydride was synthesized near x=67 (MgY2Hy). This phase exhibited a FCC-type structure with a cell parameter of a=0.516 nm. This high-pressure phase was dehydrogenated at about 600 K under an Ar atmosphere of 0.05 MPa, and the FCC structure was maintained after dehydrogenation. The amount of hydrogen desorbed at about 600 K was 1.4 mass%.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 43 (11), 2717-2720, 2002
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679224889472
-
- NII論文ID
- 130004451714
- 10012327872
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD3sXjtFen
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 6367059
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可