Formation, Thermal Stability and Mechanical Properties in Zr-Al-Co Bulk Glassy Alloys
-
- Wada Takeshi
- Graduate School, Tohoku University
-
- Zhang Tao
- Institute for Materials Research, Tohoku University
-
- Inoue Akihisa
- Institute for Materials Research, Tohoku University
この論文をさがす
抄録
A Zr–Al–Co ternary alloy was investigated in order to clarify the glass-forming ability, thermal stability and mechanical properties. The Zr55Al20Co25 alloy was found to be fabricated in bulk glassy alloy rods with diameters up to at least 2.5 mm. The glassy alloy rod of 2.5 mm in diameter exhibits a large supercooled liquid region of 79 K, followed by a nearly single exothermic peak due to the precipitation of ZrCo+ZrAlCo+Zr6Al2Co phases. The glassy alloy rod exhibits Young’s modulus of 114 GPa, high compressive fracture strength of 1900 MPa and total fracture elongation of 1.7%. The finding of forming the bulk glassy alloy at the new ternary composition of Zr55Al20Co25 by the copper mold casting method is encouraging for future search of a new glassy alloy composition.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 43 (11), 2843-2846, 2002
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204246315648
-
- NII論文ID
- 130004451733
- 10012328221
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD3sXjtFGl
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 6367485
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可