Glassy Ni-Ta-Ti-Zr(-Co) Alloys with High Thermal Stability and High Corrosion Resistance
-
- Zhang Tao
- Institute for Materials Research, Tohoku University
-
- Pang Shujie
- Institute for Materials Research, Tohoku University
-
- Asami Katsuhiko
- Institute for Materials Research, Tohoku University
-
- Inoue Akihisa
- Institute for Materials Research, Tohoku University
この論文をさがす
抄録
Glassy Ni-based alloys with high thermal stability and high corrosion resistance were synthesized in Ni-Ta-Ti-Zr(-Co) alloy system. Glassy Ni60Ta40−x−yTixZry alloys exhibit supercooled liquid region exceeding 50 K in a wide composition range and the largest supercooled liquid region of 67 K was obtained at Ni60Ta20Ti15Zr5. Glassy Ni55Ta20Ti10Zr8Co7 alloy exhibits the highest thermal stability among the Ni-based glassy alloys reported up to date, which is evidenced by its high Tg and Tx of 899 K and 977 K, respectively, and a larger supercooled liquid region of 78 K. Bulk glassy Ni55Ta20Ti10Zr8Co7 alloy in a rod form with a diameter of 1 mm can be prepared by copper mold casting. The glassy Ni-Ta-Ti-Zr(-Co) alloys are spontaneously passivated with low passive current density in 1 N H2SO4 and 1 N HCl solutions and their corrosion rate was less than 0.1 μm/year in the above solutions.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 44 (11), 2322-2325, 2003
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679222227328
-
- NII論文ID
- 130004451961
- 10012537817
- 30018850316
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD3sXpvFarsrc%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 6752800
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可