Relationship between Deformation and Recrystallization Structures in Fe-Si Single Crystal and Containing {111}<112> Grain

DOI Web Site Web Site 被引用文献4件 参考文献19件

書誌事項

タイトル別名
  • Relationship between Deformation and Recrystallization Structures in Fe-Si Single Crystal and Bicrystal Containing {111}‹112› Grain
  • Relationship between Deformation and Recrystallization Structures in Fe-Si Single Crystal and Bicrystal Containing {111}&lsaquo;112&rsaquo; Grain

この論文をさがす

抄録

To study the relationship between slip morphology and recrystallization of body centered cubic metals, an Fe-3%Si alloy single crystal sample of {111}‹112› orientation and a bicrystal sample having {111}‹112› and {001}‹110› component grains were deformed in tension and subsequently annealed. Both samples exhibited necking at the beginning of plastic deformation. The appearance of slip bands was totally different in the component grains of the bicrystal sample. Straight slip bands aligned along the traces of two {110} slip planes were observed in the {111}‹112› grain. On the other hand, wavy slip bands accompanied by high-step cross-slip were observed in the {001}‹110› grain. After annealing, the tensile-deformed single crystal sample did not recrystallize. In the bicrystal sample, recrystallized grains were formed only in the {111}‹112› grain. The difficulty in recrystallization of tensile-deformed samples is discussed in relation to the tendency to cross-slip.

収録刊行物

被引用文献 (4)*注記

もっと見る

参考文献 (19)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ