- A Mechano-Chemical Synthesis of Lthium-lon Conductive Amorphous Materials in the System Li2S-GeS2
- リチウム イオン デンドウセイ Li2S GeS2ケイ ヒショウシツ ザイリョウ ノ メカニカルミリングホウ ニ ヨル ゴウセイ
この論文をさがす
抄録
Lithium-ion-conducting amorphous materials in the system Li2S-GeS2 were prepared by use of a high-energy ball-milling process. The amorphous materials were obtained over the wide composition range up to 66.7mol%Li2S content. The composition range in which the amorphous materials were obtained by the ball-milling process was much wider than the glass-forming region by conventional melt-quenching methods. The lithium-ion conductivities of the obtained amorphous materials increased with an increase in the Li2S content. The activation energies for conduction correspondingly decreased with increasing the Li2S content. The 66.7Li2S⋅33.3GeS2(mol%) sample showed the maximum conductivity 1.1×10-4Scm-1 at 298 K.DC polarization measurements suggested that a lithiumion transport number was almost unity for the obtained amorphous materials.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 51 (4), 211-216, 2004
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206309434368
-
- NII論文ID
- 10012886869
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 6935576
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可