Orientation Relationships of Icosahedral Quasicrystalline Phase and Laves Phase Precipitates in a Ferritic Alloy
-
- Yamamoto Keisuke
- Department of Materials Science and Engineering, Tokyo Institute of Technology
-
- Kimura Yoshisato
- Department of Materials Science and Engineering, Tokyo Institute of Technology
-
- Mishima Yoshinao
- Department of Materials Science and Engineering, Tokyo Institute of Technology
この論文をさがす
抄録
The precipitation behavior and orientation relationships of icosahedral quasicrystalline phase (I-phase) and Laves phase precipitates in ferrite matrix have been investigated by transmission electron microscopy (TEM) in an Fe-10Cr-1.4W-4.5Co-0.3Si (at%) alloy. It is found that the precipitates of the alloy aged at 873 K are the I-phase but those of the alloy aged at 973 K are the Laves phase. Through a double aging experiment at both temperatures, it is shown that the transformation between the I-phase and the Laves phase occurs. Although a single orientation relationship is established between the I-phase and the ferrite matrix, three different types of the orientation relationships between the Laves phase and the ferrite matrix are obtained by the analysis of SAD patterns. The results can be explained by the coincidence between the five-fold symmetrical plane of the I-phase and the (1120) plane of the Laves phase on the phase transformation between them.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 45 (8), 2598-2601, 2004
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204251969792
-
- NII論文ID
- 130004452529
- 10013474299
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD2cXosV2ht78%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 7051470
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可