Crystalline Texture and Magnetostriction in Rapid-Solidified Fe-Pd Alloy Ribbons
-
- Onoki Takamasa
- Graduate School of Engineering, Tohoku University
-
- Yamaura Shin-ichi
- Institute for Materials Research, Tohoku University
-
- Furuya Yasubumi
- Faculty of Science and Engineering, Hirosaki University
-
- Kimura Hisamichi
- Institute for Materials Research, Tohoku University
-
- Matsuzaki Takashi
- Graduate School of Engineering, Tohoku University
-
- Watanabe Tadao
- Graduate School of Engineering, Tohoku University
この論文をさがす
抄録
Rapid-solidified ferromagnetic shape memory Fe-30.2 at. %Pd alloy ribbon has a large magnetostriction more than 1.0 × 10−3 (= 1000 μ-strain). This type of magnetostriction is caused by the re-arrangements of martensitic twins (i.e., variants) by the applied magnetic field, therefore, it is generally very sensitive to the crystalline texture and twin's morphology of material. In order to develop a more high performance magnetostrictive actuator material driven by smaller magnetic field, the effect of grain and twin boundary microstructures on megnetostriction was studied by changing the condition of heat treatments. For the sample with strongly (100) textured grains after oil-bath quenching, a steep increment and large strain of 0.7 × 10−3 was induced at a fairly low magnetic field of 35 k A·m−1 (= 1.5 kOe) when the magnetic field was applied normal to the ribbon surface. On the other hand, for the sample with randomly oriented grains and excessive existence of twin boundaries by ice-water quenching after long time annealing, the induced strain was initially small and then it gradually increased up to 0.6 × 10−3 at 70kA·m−1. This difference of sensitivity in magnetostriction behavior is discussed from the viewpoint of magnetic domain mobility in connection with grain and twin boundary microstructures.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 45 (11), 3120-3123, 2004
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204250154624
-
- NII論文ID
- 130004452310
- 10014124382
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD2MXhtVShtLk%3D
-
- ISSN
- 13475320
- 13459678
- http://id.crossref.org/issn/09161821
-
- NDL書誌ID
- 7162775
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可