Fabrication of Lotus-Type Silver with Directional Pores by Unidirectional Solidification in Oxygen Atmosphere
-
- Nakahata Takuji
- The Institute of Scientific and Industrial Research, Osaka University
-
- Nakajima Hideo
- The Institute of Scientific and Industrial Research, Osaka University
この論文をさがす
抄録
Lotus-type silver was fabricated by unidirectional solidification in mixture gas of oxygen and argon at high pressures. Two solidification methods were adopted in this study: the unidirectional solidification casting method and the Czochralski method. The directional pores were evolved by insoluble oxygen when silver melt dissolving oxygen was solidified. Non-uniform size distributions of pores in distorted shapes were observed in lotus-type silver fabricated by the unidirectional solidification casting method. On the other hand, round shape pores with good circularity and more uniform pore size were found in the cross section of the lotus-type silver made by the Czochralski method. The distortion of pore shape is attributed to the re-dissolution of oxygen gas in the pores to the molten silver during solidification.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 46 (3), 587-592, 2005
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204251070336
-
- NII論文ID
- 10015579100
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD2MXjvFSru7g%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 7289930
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可