Effect of adding elements on creep rupture strength and toughness for heat resistant 12%Cr steel of 1300°C class gas turbine disc was investigated. Creep rupture strength was increased by addition of Mo, W, V, Nb, and N. It was found that the addition of Nb causes a significant increase of creep rupture strength due to fine dispersion of NbC and of ductility due to grain refining. Chemical composition of 12Cr-2.5Ni-2Mo-0.2V-0.08Nb-N steel is determined for gas turbine disc application. Preparation of real scale disc was carried out by electro-slag remelting process in order to avoid the segregation of adding elements in ingot. It is resulted that the mechanical properties of real scale disc specimen show the equivalent properties of small specimens. The steel discs for gas turbine were manufactured from the new steel.
収録刊行物
-
- ISIJ International
-
ISIJ International 35 (11), 1400-1406, 1995
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206451786752
-
- NII論文ID
- 10015615762
-
- NII書誌ID
- AA10680712
-
- ISSN
- 13475460
- 09151559
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可