High Nitrogen Steels. Relationship between Pitting and Intergranular Corrosion of Nitrogen-bearing Austenitic Stainless Steels.

DOI Web Site 3 Citations 35 References

Search this article

Abstract

Nitrogen-bearing types 304 and 316 stainless steels thermally aged at 823, 873 and 923 K for various durations were investigated to understand the relation between the sensitized microstructure (intergranular corrosion) and pitting corrosion resistance. The sensitized microstructure was assessed as per ASTM A262 practice A (electrolytic etch test) and electrochemical potentiokinetic reactivation (EPR) tests; and pitting corrosion resistance was evaluated in an acidic chloride medium by potentiodynamic anodic polarization method. The results indicated that the pitting resistance decreased as the degree of sesitization increased, and this was attributed to the formation of a heterogeneous microstructure consisting of Cr-rich M23C6 carbides, Cr-depleted regions and the carbide/matrix interfaces resulting from the sensitizing treatment. Pitting attack was found at triple points, grain boundaries and precipitate/matrix interfaces. Time-temperature-sensitization-pitting diagrams were developed for both the alloys based on the results, interrelating the sensitized microstructure and the pitting attack.

Journal

  • ISIJ International

    ISIJ International 36 (7), 799-806, 1996

    The Iron and Steel Institute of Japan

Citations (3)*help

See more

References(35)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top