High Nitrogen Steels. Nitrogen Bearing Martensitic Stainless Steels: Microstructure and Properties.
-
- Horovitz M. B.
- Departamento de Engenharia Metalúrgica e de Materiais, Universidade de São Paulo
-
- Neto F. Beneduce
- Institute de Pesquisas Tecnológicas do Estado de São Paulo
-
- Garbogini A.
- Departamento de Engenharia Metalúrgica e de Materiais, Universidade de São Paulo
-
- Tschiptschin A. P.
- Departamento de Engenharia Metalúrgica e de Materiais, Universidade de São Paulo
この論文をさがす
抄録
Three experimental nitrogen bearing martensitic stainless steels (nitrogen content ranging from 1600 to 1900 ppm) were produced in an air induction furnace and the N was added into the melt as Fe-Cr-N master alloy or gas nitrogen. These alloys with (C+N) content equal to 0.32 wt% were compared with a commercial AISI 420 steel. The alloys were homogenized, forged, quenched in air (alloys I and II) or in oil (alloys III and AISI 420) from temperatures between 1073 to 1423 K. The austenitizing temperature of 1273 K was chosen and the specimens were tempered in the range of 373 to 973 K for 1 h. SEM of the 773 K tempered nitrogen steels did not show any visible precipitates. The AISI 420 alloy, however, exhibited a high density of chromium carbide precipitates when heat treated in the same manner. TEM observation of the alloy III did not show clearly fine and well distributed precipitates. The nitrogen bearing steels showed better corrosion resistance in the 773 K tempered condition than the as quenched AISI 420 as a consequence of lower precipitate size, stoichiometry and distribution of precipitates.
収録刊行物
-
- ISIJ International
-
ISIJ International 36 (7), 840-845, 1996
一般社団法人 日本鉄鋼協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681430195072
-
- NII論文ID
- 10015618385
-
- NII書誌ID
- AA10680712
-
- COI
- 1:CAS:528:DyaK28XksFSktL4%3D
-
- ISSN
- 13475460
- 09151559
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可