- WAKI Hiroyuki
- Department of Mechanical Science and Bioengineering, Osaka University
-
- OGURA Keiji
- Department of Mechanical Science and Bioengineering, Osaka University
-
- NISHIKAWA Izuru
- Department of Mechanical Engineering, Osaka Institute of Technology
-
- KASHIHARA Yoshihiko
- Corporate Business Strategy Division, KYOCERA Corporation
この論文をさがす
抄録
Residual stresses of plasma sprayed coatings, NiCr alloy, CoNiCrAlY alloy, Al2O3 ceramics and ZrO2-8%Y2O3 ceramics, were measured in this study. SACHS method with a strain gauge was used to measure the residual stress. Type 304 stainless steel and mild steel were selected for the substrates. The results obtained were summarized as follows: 1) Tensile residual stresses were generated in plasma sprayed coatings. 2) The values of residual stress in ceramics coatings were relatively small and the values took lower than 40MPa. 3) Tensile residual stress values of metallic alloy coatings on mild steel substrates were higher than those on type 304 stainless steel substrates. 4) Residual stresses in Low Pressure Plasma Sprayed (LPPS)-coatings were larger than those in Atmospheric Plasma Sprayed (APS)-coatings. 5) Pre-heating of a substrate will effectively reduce tensile residual stress in a coating.
収録刊行物
-
- JSME International Journal Series A Solid Mechanics and Material Engineering
-
JSME International Journal Series A Solid Mechanics and Material Engineering 46 (4), 590-597, 2003
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206493774848
-
- NII論文ID
- 10016192033
-
- NII書誌ID
- AA11179396
-
- ISSN
- 13475363
- 13447912
-
- NDL書誌ID
- 6713387
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可