Glass Formation and Thermal Stability of Bulk Glassy Cu–Zr–Ti–Sn–Si Alloys
書誌事項
- タイトル別名
-
- Glass Formation and Thermal Stability of Bulk Glassy Cu–Zr–Ti–Sn–Si Alloys
この論文をさがす
抄録
The new Cu-based bulk glassy alloys in Cu–Zr–Ti–Sn–Si alloy system were formed by copper mold casting. The critical diameter for glass formation is 5 mm for Cu50Zr42.5Ti7.5, and increases to 6 mm for (Cu0.5Zr0.425Ti0.075)99Sn1 and 7 mm for (Cu0.5Zr0.425Ti0.075)98.8Sn0.6Si0.6. The minor addition of Sn or Sn and Si in Cu50Zr42.5Ti7.5 causes an increase in the supercooled liquid region from about 40 K to about 50 K, and in the reduced glass transition temperature from about 0.59 to about 0.60.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 46 (7), 1692-1694, 2005
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679228200576
-
- NII論文ID
- 10016619859
- 30018851303
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD2MXpvFWksrY%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 7371223
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可