- Magnetic Properties of Ba-Pr-Co M-type Ferrite Fine Particles Prepared by Controlling the Chemical Coprecipitation Method and Heat Treatment
- 化学的共沈法によるBa-Pr-Co系M型フェライト微粒子の磁気特性
- カガクテキ キョウチンホウ ニ ヨル Ba Pr Coケイ Mガタ フェライト ビリュウシ ノ ジキ トクセイ
この論文をさがす
抄録
Single phase Ba-Pr-Co M-type ferrite fine particles were prepared by controlling the chemical coprecipitation method and subsequent heat treatment. The chemical reagents used for this experiment were BaCl2·2H2O, FeCl3·6H2O, PrCl3·7H2O and CoCl2·6H2O. The chemical coprecipitation compositions were chosen according to the formula {(BaO)·n/2(Fe2O3)}100−x−y(Pr2O3)x(CoO)y, where n was fixed at 10.5, x was varied between 1.0 and 12.0, y between 2.0 and 10.0. A water solution containing Ba2+, Fe3+, Pr3+ and Co2+ was poured into a solution of NaOH (pH=13.0). The precipitated products were boiled at 100°C for 2h, and they were carefully washed with pure water for 24h. The washing was repeated 5 times and the products were then filtered and dried at 80°C for 12h. The obtained fine particles were heated at a temperature between 950 and 1100°C for 2h in air to get single phase Ba-Pr-Co M-type ferrite fine particles. The most prominent magnetic properties have been observed for the sample with the preparation composition of {(BaO)·5.25(Fe2O3)}92.0(Pr2O3)4.0(CoO)4.0 ; they are as follows: σs=83.1×10−6 Wb·m/kg (66.1 emu/g), σr=41.0×10−6 Wb·m/kg (32.6 emu/g), HcJ=467.8 kA/m (5.88 kOe), α(σr)=−0.19 %/°C, α(HcJ)=0.07 %/°C and Tc=450°C.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 53 (7), 610-616, 2006
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681284913408
-
- NII論文ID
- 10018005704
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 8046100
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可