X-ray Photoemission Spectroscopy and Magnetic Properties of Bi Doped LaMnO3
-
- OGAWA Takashi
- Graduate School of Engineering, Tokai University
-
- SHINDO Haruo
- Graduate School of Engineering, Tokai University
-
- TAKEUCHI Hiromasa
- Graduate School of Engineering, Tokai University
-
- KOIZUMI Yoshiharu
- Graduate School of Engineering, Tokai University
Bibliographic Information
- Other Title
-
- Bi添加LaMnO3のXPS分析と磁性
- Bi テンカ LaMnO3 ノ XPS ブンセキ ト ジセイ
Search this article
Abstract
Perovskite-type La1−xBixMnO3 (LBMO), which are prepared by doping the Bismuth (Bi) ion in LaMnO3, were shown to exhibit the colossal magnetoresistance (CMR) effect. Samples were produced using a sintering process in an air atmosphere as a function of the Bi composition ratio x. X-ray diffraction measurements showed that the LBMO crystal structure varied among an orthorhombic (or rhombohedral) type with 0.0<x<0.3, to a cubic type with 0.3<x<0.5, and to a monoclinic type with for 0.5<x. The CMR effect of LBMO for x=0.2 was approximately 400% at 140 K. In addition, the magnetoresistance of the LBMO system was found to be proportional to the square of the magnetization. It was interpreted that, from XPS analysis, the valence states of manganese and bismuth atoms in LBMO contain [Mn3+,Mn4+] and [Bi3+, Bi2+ (or pseudo-divalent Bismuth)] ionic states.
Journal
-
- Hyomen Kagaku
-
Hyomen Kagaku 27 (9), 511-517, 2006
The Surface Science Society of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390001206457755136
-
- NII Article ID
- 10018051649
-
- NII Book ID
- AN00334149
-
- COI
- 1:CAS:528:DC%2BD28Xht1Wgtr3L
-
- ISSN
- 18814743
- 03885321
-
- NDL BIB ID
- 8091007
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed