書誌事項
- タイトル別名
-
- Application of MgO-C Brick to Ruhrstahl Heraus Lower Vessel
- Ruhrstahl Heraus カブ ソウ エ ノ MgO Cレンガ ノ テキヨウ
この論文をさがす
抄録
In order to improve the characteristics of MgO-C brick applied to RH lower vessel, several originally-prescribed specimens were prepared by changing the amount of additives with different size distributions. These specimens were tested on their durabilities with an experimental rotary type electric furnace and a practical 2RH in a manufacturing line. Following are the major results:<br>1) Specimens prepared with 3-7% expanded carbon and anti-oxidation agents exhibited excellent spalling durability.<br>2) Specimens containing both metallic Al and metallic Si had higher elasticity than those containing only metallic Al and those with a higher Si content retained excellent durability against corrosion and oxidation.<br>3) Corrosion at a high temperature was suppressed by removing SiC from the low C-content MgO-C specimen.<br>4) Durability against spalling was improved by shifting the size distribution of specimen from fine one to coarse one.
収録刊行物
-
- 粉体工学会誌
-
粉体工学会誌 43 (9), 676-681, 2006
一般社団法人 粉体工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204512163200
-
- NII論文ID
- 10018074763
-
- NII書誌ID
- AN00222757
-
- ISSN
- 18837239
- 03866157
-
- NDL書誌ID
- 8093984
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可