Standard Gibbs Energy of Formation of Zn8La Determined by Solution Calorimetry and Measurement of Heat Capacity from Near Absolute Zero Kelvin
-
- Morishita Masao
- Department of Materials Science and Chemistry, University of Hyogo
-
- Yamamoto Hiroaki
- Department of Materials Science and Chemistry, University of Hyogo
-
- Tsuboki Kohei
- Department of Materials Science and Chemistry, University of Hyogo
-
- Matsumoto Yasutomo
- Department of Materials Science and Chemistry, University of Hyogo
書誌事項
- タイトル別名
-
- Standard Gibbs Energy of Formation of Zn<SUB>8</SUB>La Determined by Solution Calorimetry and Measurement of Heat Capacity from Near Absolute Zero Kelvin
この論文をさがす
抄録
The thermodynamic properties of Zn8La were investigated by calorimetry. The standard entropy of formation at 298 K, ΔfS298°, was determined from measuring the heat capacities, Cp, from near absolute zero (2 K) to 300 K by the relaxation method. The standard enthalpy of formation at 298 K, ΔfH298°, was determined by solution calorimetry in hydrochloric acid solution. The standard Gibbs energy of formation at 298 K, ΔfG298°, was determined from these data. The results obtained were as follows: ΔfH298°(Zn8La)/kJ·mol−1 = −297.18±18; ΔfS298°(Zn8La)/J·mol−1·K−1 = −25.02±3.60; ΔfG298°(Zn8La)/kJ·mol−1 = −289.71±18. The coefficient, γ, of the electronic term contributing to the heat capacity of Zn8La was small, indicating that decrease of the density of states for 4f component of the lanthanum atom in the vicinity of EF.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 47 (6), 1555-1559, 2006
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679227486976
-
- NII論文ID
- 130004453169
- 10018160630
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 7951101
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可