Standard Gibbs Energy of Formation of Zn<SUB>8</SUB>La Determined by Solution Calorimetry and Measurement of Heat Capacity from Near Absolute Zero Kelvin
-
- Morishita Masao
- Department of Materials Science and Chemistry, University of Hyogo
-
- Yamamoto Hiroaki
- Department of Materials Science and Chemistry, University of Hyogo
-
- Tsuboki Kohei
- Department of Materials Science and Chemistry, University of Hyogo
-
- Matsumoto Yasutomo
- Department of Materials Science and Chemistry, University of Hyogo
Bibliographic Information
- Other Title
-
- Standard Gibbs Energy of Formation of Zn8La Determined by Solution Calorimetry and Measurement of Heat Capacity from Near Absolute Zero Kelvin
Search this article
Abstract
The thermodynamic properties of Zn8La were investigated by calorimetry. The standard entropy of formation at 298 K, ΔfS298°, was determined from measuring the heat capacities, Cp, from near absolute zero (2 K) to 300 K by the relaxation method. The standard enthalpy of formation at 298 K, ΔfH298°, was determined by solution calorimetry in hydrochloric acid solution. The standard Gibbs energy of formation at 298 K, ΔfG298°, was determined from these data. The results obtained were as follows: ΔfH298°(Zn8La)/kJ·mol−1 = −297.18±18; ΔfS298°(Zn8La)/J·mol−1·K−1 = −25.02±3.60; ΔfG298°(Zn8La)/kJ·mol−1 = −289.71±18. The coefficient, γ, of the electronic term contributing to the heat capacity of Zn8La was small, indicating that decrease of the density of states for 4f component of the lanthanum atom in the vicinity of EF.
Journal
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 47 (6), 1555-1559, 2006
The Japan Institute of Metals and Materials
- Tweet
Details 詳細情報について
-
- CRID
- 1390282679227486976
-
- NII Article ID
- 130004453169
- 10018160630
-
- NII Book ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL BIB ID
- 7951101
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed