The Stress Induced Hydrogen Diffusion Behavior and the Sensitivity of Hydrogen Embrittlement at the Heat Affected Zone of Weld Part Based on Analytical Solution

DOI IR HANDLE Web Site Web Site 1 Citations 28 References

Bibliographic Information

Other Title
  • 解析解による溶接ＨＡＺ部の応力誘起水素拡散挙動解析と水素感受性評価
  • カイセキカイ ニ ヨル ヨウセツ HAZブ ノ オウリョク ユウキ スイソ カクサン キョドウ カイセキ ト スイソ カンジュセイ ヒョウカ

Search this article

Abstract

  The analytical solution of hydrogen diffusion and concentration around the heat affected zone of weld part was derived by taking account for the effect of residual stress on hydrogen concentration. Based on the theoretical analysis, the sensitivity of hydrogen embrittlement was formulated and it is proportional to DK2, where D is diffusion coefficient, K is stress gradient term of residual stress approximated by linear function. It was in good agreement with that previously obtained by numerical analysis.<br>    This result shows that the law of hydrogen sensitivity is commonly valid independent of boundary condition when the distribution of residual stress is approximately written by linear functions of the distance in the heat affected zone. Furthermore the analysis of the period when hydrogen embrittlement becomes remarkable was conducted. This result enables us to predict the behavior of hydrogen embrittlement at the heat affected zone of weldment.<br>

Journal

Citations (1)*help

See more

References(28)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top