木炭・竹炭のミクロ孔構造 : 測定方法の確立と細孔制御の可能性 Micropore Structure of Wood and Bamboo Charcoals : Establishment of a method for the calculation of effective pore size distribution and the possibility of controlling micropore structure

この論文にアクセスする

この論文をさがす

著者

    • 秋友 水季 AKITOMO Mizuki
    • 京都府立大学大学院農学研究科 Research Division of Agriculture, Graduate School of Kyoto Prefectural University
    • 鈴木 里佳 SUZUKI Rika
    • 京都府立大学大学院農学研究科 Research Division of Agriculture, Graduate School of Kyoto Prefectural University
    • 飯田 生穂 IIDA Ikuho
    • 京都府立大学大学院農学研究科 Research Division of Agriculture, Graduate School of Kyoto Prefectural University
    • 古田 裕三 FURUTA Yuzo
    • 京都府立大学大学院農学研究科 Research Division of Agriculture, Graduate School of Kyoto Prefectural University

抄録

木炭・竹炭の細孔径分布について信頼性の高い測定方法を確立するため,氷水温度(273 K)での二酸化炭素の吸着実験を行った。得られた吸着等温線をHK法(Horvath-Kawazoe法)により解析し,細孔径分布を得た。本法は従来の方法よりも高温測定であるため,吸着平衡に要する時間が短縮され,再現性の高い細孔径分布が得られた。木炭・竹炭のミクロ細孔径分布のピークは0.5 nm付近に存在し,これらはグラファイト構造に類似の層状構造の乱れに起因する細孔と考えられた。この結果と,木炭・竹炭にはメソ孔は存在しないとの既往の研究結果から,これらのミクロ孔が,相対湿度域40~60%における炭の吸湿性の著しい増大に関与していることが明らかとなった。<br>さらに,木炭・竹炭のミクロ細孔構造制御の可能性について検討するため,ポリエチレングリコール(PEG)処理後に炭化した試料の細孔径分布を同様の方法で求めたところ,わずかながら細孔の拡大が認められた。

Adsorption of CO<sub>2</sub> gas onto charcoals was studied at the ice-water temperature (273 K) in order to establish a method for a reliable determination of pore size distributions in charcoals from wood and bamboo. The pore size distributions were determined by analyzing adsorption isotherms using the HK method (Horvath-Kawazoe method). The pore size distributions obtained were highly reproducible and reliable, and peaks of pore size distributions in the charcoals were found at about 0.5 nm. Based on size, these micropores in charcoals were judged to result from a disordered-graphite-like structure. It was previously found that wood and bamboo charcoals have only a small amount of mesopores and no peak of the distribution in the mesopore region. From the previous and the present results, it can be concluded that the micropores mentioned above are responsible for a steep increase found in the adsorption isotherms of water vapor in a range of about 40 to 60% relative humidity.<br>Pore size distributions were also determined for the charcoals from wood pretreated with polyethylene glycol (PEG), as an attempt to obtain some information about the possibility of controlling micropore structure in wood and bamboo charcoals. A small increase in larger pores above 0.5 nm was found in the pretreated charcoals as compared to the untreated charcoals.

収録刊行物

  • 木材学会誌  

    木材学会誌 52(4), 228-234, 2006-07-25 

    The Japan Wood Research Society

参考文献:  7件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  3件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10018204830
  • NII書誌ID(NCID)
    AN00240329
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    00214795
  • NDL 記事登録ID
    8047569
  • NDL 雑誌分類
    ZP21(科学技術--化学・化学工業--木材)
  • NDL 請求記号
    Z17-484
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ