歯冠用硬質レジンのレオロジーに関する研究 Rheological Study of Hard Resin for Crown and Bridge

この論文にアクセスする

この論文をさがす

著者

    • 泉田 明男 IZUMIDA Akio
    • 東北大学大学院歯学研究科口腔修復学講座咬合機能再建学分野 Division of Fixed Prosthodontics, Department of Restorative Dntistry, Tohoku University Graduate School of Dentistry
    • 友田 浩三 TOMOTA Kohzo
    • 東北大学大学院歯学研究科口腔修復学講座歯科生体材料学分野 Division of Dental Biomaterials, Department of Restorative Dntistry, Tohoku University Graduate School of Dentistry
    • 木村 幸平 KIMURA Kohei
    • 東北大学大学院歯学研究科口腔修復学講座咬合機能再建学分野 Division of Fixed Prosthodontics, Department of Restorative Dntistry, Tohoku University Graduate School of Dentistry
    • 小松 正志 KOMATSU Masashi
    • 東北大学大学院歯学研究科口腔修復学講座歯科保存学分野 Division of Operative Dentistry, Department of Restorative Dntistry, Tohoku University Graduate School of Dentistry
    • 奥野 攻 OKUNO Osamu
    • 東北大学大学院歯学研究科口腔修復学講座歯科生体材料学分野 Division of Dental Biomaterials, Department of Restorative Dntistry, Tohoku University Graduate School of Dentistry

抄録

目的: 各種市販歯冠用硬質レジンペーストの賦形性に影響する流動性を調べることを目的に, 各種ペーストの挙動と築盛操作時の温度依存性について検討を行った.<BR>方法: 使用材料は現在臨床で用いられている5種類の前装用硬質レジンであるニューメタカラーインフィス, ソリデックス, セラマージュ, グラディア, エステニアC&Bを使用し, 各ペーストの組成分析と流動性を調べた. 硬化前レジンペーストの粘度は, コーンプレート型回転粘度計を用いて測定を行った.<BR>結果: 各レジンペーストは非ニュートン流動を示し, 流動曲線は上昇曲線と下降曲線の異なるヒステリシス曲線を描いた. また各レジンペーストの各流動曲線 (20℃, 25℃, 30℃) における保留開始時のずり応力を測定した結果, 20℃のずり応力は25℃, 30℃ に対し有意に大きく, 25℃ のずり応力は30℃に対し有意に大きな値を示し, 低温側で粘性が高い傾向を示した. 保留前後のずり応力の比較では, エステニアC&Bを除いて, 他は全て保留前が保留後よりも有意に大きな値を示した.<BR>結論: 今回使用した各種レジンペースト全てにおいて作業温度の20-30℃ 間で温度依存性, チキソトロピー性を有していた. しかし歯冠用レジンペーストは, ペーストの種類により, 流動性に大きな差がありレジン築盛時の操作性に大きく影響を及ぼしていることが示唆された.

Purpose: For the purpose of evaluating the flow properties influencing the formativeness of commercial hard resin pastes used in the construction of crowns and bridges, we examined the behaviors of various resin pastes and their temperature dependence during manipulation.<BR>Methods: Five types of hard resins currently in use for the construction of crowns and bridges in the clinical setting, namely, New Meta Color INFIS, Solidex, Ceramage, Gradia, and Estenia C&B, were examined. The components and flow properties of each resin paste were investigated in relation to the dentine and enamel colors. The viscosities of the resin pastes before curing were measured by a cone-plate viscometer.<BR>Results: Each resin paste demonstrated a non-Newtonian flow, and the flow curve showed a hysteresis loop, in which the upward and downward curves were different. When the shear stress at the beginning of the holding time of the flow curve (20°C, 25°C, 30°C) of each resin paste was measured, the shear stress at 20°C was found to be significantly higher than that at 25°C and 30°C, and the shear stress at 25°C was found to be significantly higher than that at 30°C. The viscosity was found to be higher at lower temperatures than at higher temperatures. Comparison of the shear stresses at the beginning and at the end of the holding time revealed that the stress at the beginning of the holding time was significantly higher than that at the end of the holding time for all except the Estenia C&B resin paste.<BR>Conclusions: Each of the resin pastes used in the present study showed temperature dependence of its characteristics in the temperature range examined (20-30°C) and thixotropic fluidity. However, the flow characteristics of these resin pastes differed significantly, suggesting that the flow characteristics may affect the manipulation of resin formativeness.

収録刊行物

  • 日本補綴歯科學會雜誌 = The journal of the Japan Prosthodontic Society  

    日本補綴歯科學會雜誌 = The journal of the Japan Prosthodontic Society 50(3), 396-404, 2006-07-10 

    Japan Prosthodontic Society

参考文献:  21件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  4件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10018226286
  • NII書誌ID(NCID)
    AN00197911
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    03895386
  • データ提供元
    CJP書誌  CJP引用  J-STAGE 
ページトップへ