ラット頭頂骨における骨形成促進剤TAK-778含有β-TCPの効果 : 含有量の違いによる骨形成量の比較 Effect of β-TCP Containing the Bone-Growth Promoting Compound, TAK-778, on the Vertex Bone of Rat : Change of Volmetric Bone Formation Corresponding to the Containing Volume of TAK-778

この論文にアクセスする

この論文をさがす

著者

    • 笹澤 武史 SASAZAWA Takefumi
    • 日本歯科大学新潟歯学部歯科補綴学第2講座 Department of Crown and Bridge Prosthodontics, Nippon Dental University School of Dentistry at Niigata
    • 吉江 紀夫 YOSHIE Norio
    • 日本歯科大学新潟歯学部解剖学第2講座 Department of Oral Histology, Nippon Dental University School of Dentistry at Niigata
    • 渡邉 文彦 WATANABE Fumihiko
    • 日本歯科大学新潟歯学部歯科補綴学第2講座 Department of Crown and Bridge Prosthodontics, Nippon Dental University School of Dentistry at Niigata
    • 畑 好昭 HATA Yoshiaki
    • 日本歯科大学新潟歯学部歯科補綴学第2講座 Department of Crown and Bridge Prosthodontics, Nippon Dental University School of Dentistry at Niigata

抄録

目的: 本研究の目的は, 骨形成促進剤3-ベンゾチエピン誘導体TAK-778 (武田薬品工業) の担体としてβ-リン酸三カルシウム顆粒β-TCP (オリンパス光学) を用い, その含有量を変化させることによる骨形成量を形態組織的に検討することである.<BR>方法: 週齢SD系雌性ラットの頭頂部に切開を加え, 骨膜を剥離し頭部中央にチタンチューブをレジン系セメントにて固定した. チタンチューブ内にTAK-778とβ-TCPを混和したものを各条件で填入した. 4週後, 8週後および16週後に組織標本を作製し, 組織形態的に観察しNIHイメージにて新生骨の割合を比較検討した. 統計学的分析は, TAK-778群および各週群の要因で一元配置分散分析を行い, 各平均値間の検定にはFisherのPSLDによる多重比較 (P<0.05) を行った.<BR>結果: 形態組織観察から, 含有量, 埋入期間を問わずTAK-778含浸群すべてに新生骨を認め, 各平均値間の検定では16週β-TCP+TAK778100mgの複合体で最も多くの新生骨が認められた.<BR>結論: 1. TAK-778は, 本実験でも早期に新生骨の形成を促進することが確認できた.2. β-TCPを用いることにより, TAK-778は長期的に作用することが示唆された. 3. TAK-778とβ-TCPの割合を変化させることにより骨形成時期は異なっていた. 4. 早期の新生骨量は, TAK-778100mgよりもTAK-77810mg, および50mgが良好であった. 以上のことより, TAK-778は新生骨形成を促進し, また, β-TCPはその担体としての有用性が認められた.

Purpose: This study was conducted to histomorphologically determine the quantity of bone formation induced by TAK-778, a 3-benzothiepin derivative, (Takeda Pharmaceutical Co.Ltd.), in various amounts, using b-tricalcium phosphate granules (β-TCP; OLYMPUS Corp.) as a carrier for the osteogenetic agent.<BR>Methods: Ten-week-old female SD rats were used. An incision was made over the parietal region of the head. The cranial periosteum was ablated and a titanium tube was fixed with an adhesive resin cement to the central part of the head, through which a mixture of TAK-778 and /3-TCP was implanted under various conditions. Tissue specimens were prepared at 4, 8, and 16 weeks after the implantation for histomorphological examination, and the proportion of new bone formation was compared at fixed time points using the NIH imaging software. The amount of new bone formation was examined every week after the implantation of TAK-778 at various doses, and the mean values were compared using Fisher's PSLD test (P<0.05).<BR>Results: The histomorphological observations revealed new bone formation in all the groups, irrespective of the amount and the duration of implantation of TAK-778. A comparative study revealed that the amount of new bone formation was the largest at 16 weeks following the implantation of a mixture of /3-TCP and 100 mg of TAK-778.<BR>Conclusions: 1. The present study confirmed the acceleration of new bone formation soon after TAK-778 implantation. 2. The results suggested that the action of TAK-778 could be maintained over time if the agent was used in combination with β-TCP. 3. The time-course of bone formation differed depending on the proportion of TAK-778 and β-TCP in the mixture used. 4. TAK-778 at the dose of 10 mg or 50 mg was more effective than that at the dose of 100 mg for the early formation of new bone. These results indicate that TAK-778 accelerates the formation of new bone and that β-TCP is a useful carrier for TAK-778.

収録刊行物

  • 日本補綴歯科學會雜誌 = The journal of the Japan Prosthodontic Society  

    日本補綴歯科學會雜誌 = The journal of the Japan Prosthodontic Society 50(3), 422-431, 2006-07-10 

    Japan Prosthodontic Society

参考文献:  24件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  1件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10018226390
  • NII書誌ID(NCID)
    AN00197911
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    03895386
  • データ提供元
    CJP書誌  CJP引用  J-STAGE 
ページトップへ