プラズマ照射-ポスト重合法で感温性ポリマーをグラフトしたPETフィルムの調製とHeLa細胞の温度刺激はく離 Preparation of Thermo-sensitive Polymer-grafted Poly(ethyleneterephthalate) Films by Ar Plasma Irradiation-post Polymerization Technique and Thermal Stimuli-exfoliation of HeLa Cells on Their Films

この論文にアクセスする

この論文をさがす

著者

    • 白石 浩平 SHIRAISHI Kohei
    • 近畿大学工学部生物化学工学科 Department of Biotechnology and Chemistry, School of Engineering, Kinki University
    • 大段 恵 OHDAN Megumi
    • 近畿大学大学院工業技術研究科物質化学専攻 Major in Material Chemistry, Graduate School of Industrial Technology, Kinki University
    • 前田 和磨 [他] MAEDA Kazuma
    • 近畿大学大学院工業技術研究科物質化学専攻 Major in Material Chemistry, Graduate School of Industrial Technology, Kinki University
    • 杉山 一男 SUGIYAMA Kazuo
    • 近畿大学工学部生物化学工学科 Department of Biotechnology and Chemistry, School of Engineering, Kinki University
    • 細谷 浩史 HOSOYA Hiroshi
    • 広島大学大学院理学研究科生物科学専攻 Department of Biological Science, Graduate School of Science, Hiroshima University

抄録

生体親和性に優れたpoly[<i>N</i>-(2-hydroxypropyl)methacrylamide][poly(HPMA)]を用いた機能性ヒドロゲル材料開発の一環として, 細胞増殖およびはく離用基材としての応用を検討した. メタクリル酸メチル (MMA) 成分の共重合によって温度応答性を付与したpoly (HPMA) コポリマー[poly(HPMA-<i>co</i>-MMA)]をArプラズマ照射-ポスト重合法によってポリエチレンテレフタレート (PET) フィルム上にグラフト重合した. また, 得られたフィルム (g-PET-I : グラフト量0.125mg cm<sup>-2</sup>) と比較するため, 温度応答性を有するpoly(<i>N</i>-isopropylacrylamide)[poly-(NiPAAm)]をグラフトしたPETフィルム (g-PET-II : グラフト量0.109mg cm<sup>-2</sup>) も同時に調製した. 37℃でg-PET-I, g-PET-II上でのHeLa細胞の接着・増殖は市販組織培養用ポリスチレンとほぼ同程度であった. 4℃で, 2h放置後, 接着HeLa細胞はg-PET-I上では73%, g-PET-IIでは45%がはく離した. 温度によってはく離した細胞が再培養によって増殖したことから, g-PET-Iは細胞培養および温度刺激によるはく離が知られるpoly (NiPAAm) をグラフトしたg-PET-IIに類似した細胞培養および温度刺激はく離の性能を認めた.

In order to develop a novel cell cultured material capable of thermal stimulating cell detachment from its surface, we studied the biocompatible and thermosensitive copolymer consisting of <i>N</i>-(2-hydroxypropyl) methacrylamide (HPMA) and methyl methacrylate (MMA) [poly(HPMA-<i>co</i>-MMA) : HPMA/MMA = 100/27.6 (molar ratio)]. With <i>N</i>-isopropylacylamide (NiPAAm) as a control of thermosensitive polymer, the copolymers were grafted onto poly (ethyleneterephthalate) (PET) by Ar plasma irradiation-post polymerization technique. From the contact angle (θ) measurements to water at 25°C, the θ values of poly (HPMA-<i>co</i>-MMA) grafted PET (g-PET-I: amount of grafted polymer = 0.125 mg cm<sup>-2</sup>) and poly (NiPAAm) grafted PET (g-PET-II: 0.109 mg cm<sup>-2</sup>) decreased from θ = 80° (the original PET) to θ = 52° and θ = 50°, respectively. HeLa cells attached and proliferated on g-PET-I and g-PET-II at 37°C, above the lower critical solution temperature of poly (HPMA-<i>co</i>-MMA). After the cultivation of HeLa cells, the thermal stimuli-exfoliation was also examined at 4°C for 2 h. The ratios of the number of thermal stimuli-exfoliation cells to the total number of attached cells on g-PET-I or g-PET-II were 73% and 45%, respectively, while little thermal stimuli-exfoliation was observed in the case of untreated PET.

収録刊行物

  • 高分子論文集  

    高分子論文集 63(9), 613-620, 2006-09-25 

    The Society of Polymer Science, Japan

参考文献:  21件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10018244386
  • NII書誌ID(NCID)
    AN00085011
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    03862186
  • NDL 記事登録ID
    8518712
  • NDL 雑誌分類
    ZP16(科学技術--化学・化学工業--高分子化学・高分子化学工業)
  • NDL 請求記号
    Z17-92
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ