- Effects of Substrate for Sintering on the Mechanical Properties of Injection Molded Ti-6Al-4V Alloy
- MIM Ti-6Al-4V合金における焼結敷板の機械的特性に及ぼす影響
- MIM Ti 6Al 4V ゴウキン ニ オケル ショウケツ シキイタ ノ キカイテキ トクセイ ニ オヨボス エイキョウ
この論文をさがす
抄録
Ti and Ti alloys show superior properties of lightweight, high strength and corrosion resistance, etc. Since Ti is very active at high temperature, the mechanical properties may be poor due to the oxygen and carbon contamination caused by type of substrate at high temperature and long time sintering. In this study, the effects of substrate for sintering on the mechanical properties of injection molded Ti-6Al-4V alloy were investigated using two types of substrates such as ZrO2 and Y2O3 (as-received or baked in vacuum).<BR>The relative density, microstructure and hardness of sintered compacts were changed hardly, but the tensile properties were changed by baking treatment and type of substrate for sintering. The oxygen content of the sintered compacts by using as-received ZrO2 substrate increased with increasing sintering time, then the elongation of the compacts were reduced. While the compacts using the baked ZrO2 and Y2O3 substrates showed good tensile properties because of low carbon and oxygen content.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 53 (9), 755-759, 2006
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206307534464
-
- NII論文ID
- 10018247077
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DC%2BD28XhtVOhu7bI
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 8519059
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可