Development of an Electrophoretic Sol-Gel Coating Process for Porous Metals
-
- Inoue Masahiro
- The Institute of Scientific and Industrial Research, Osaka University
-
- Hyun Soong-Keun
- The Institute of Scientific and Industrial Research, Osaka University
-
- Suganuma Katsuaki
- The Institute of Scientific and Industrial Research, Osaka University
-
- Nakajima Hideo
- The Institute of Scientific and Industrial Research, Osaka University
この論文をさがす
抄録
An electrophoretic sol-gel coating process was developed for applying to surface modification of metallic materials with complicated shapes such as porous metals. In this process, sol-gel transformation is directly induced on the substrates. In the present work, the formation of TiO2 coating layer on SUS 304 substrates is discussed as a practical example of the coating process. The colloidal particles derived from hydrolysis of titanium tetraisopropoxide in ethanol can be deflocculated using a small amount of CaCl2 to form a transparent solution. When a dc voltage of 1–5 V was applied between the substrate (cathod) and counter electrode in this solution, the gel film was formed on the substrate. After subsequent water-soaking and annealing processes, the coating layers with no cracking were obtained successfully on the substrate. As the results of X-ray photoelectron spectroscopy, the coating layers were found to consist of TiO2 doped with Ca2+ ions.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 47 (9), 2161-2166, 2006
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679227587328
-
- NII論文ID
- 130004453281
- 10018248601
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 8061701
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可