Magnetic Properties of Mechnically Milled Sm-Co Permanent Magnetic Materials with the TbCu7 Structure
-
- Joseyphus Raphael Justin
- Materials Science Centre, Department of Nuclear Physics, University of Madras Graduate School of Environmental Studies, Tohoku University
-
- Narayanasamy Alwarramanujam
- Materials Science Centre, Department of Nuclear Physics, University of Madras
-
- Gopalan Raghavan
- Defence Metallurgical Research Laboratory
-
- Chandrasekaran Venkatasubramanian
- Defence Metallurgical Research Laboratory
-
- Jeyadevan Balachandran
- Graduate School of Environmental Studies, Tohoku University
-
- Tohji Kazuyuki
- Graduate School of Environmental Studies, Tohoku University
書誌事項
- タイトル別名
-
- Magnetic Properties of Mechanically Milled Sm-Co Permanent Magnetic Materials with the TbCu<SUB>7</SUB> Structure
- Magnetic Properties of Mechanically Milled Sm-Co Permanent Magnetic Materials with the TbCu7 Structure
この論文をさがす
抄録
The magnetic properties of Sm(Co,Fe,Cu,Zr)7 compound with the TbCu7 structure are studied for the mechanically milled samples. The coercivity could be varied, without affecting the saturation magnetization, from 44 kA/m for the micron sized particles to 280 kA/m by reducing the particle size to sub-micron size (600–900 nm) using high-energy ball milling. The enhancement in the coercivity is attributed to the particles approaching single domain size. The presence of dipolar coupling suggests that the grain sizes are well above the exchange length for the milled samples. The thermal measurements indicate that the compound with the TbCu7 structure is not stable at high temperatures beyond 743 K.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 47 (9), 2264-2268, 2006
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679227616256
-
- NII論文ID
- 10018248892
- 130004453299
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- HANDLE
- 10097/52096
-
- NDL書誌ID
- 8061908
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- IRDB
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可