Temperature-Time-Transformation Curve and Viscous Flow Deformation of Zr55Cu30Al10Ni5 Bulk Glassy Alloy
-
- Zhu Shengli
- Institute for Materials Research, Tohoku University
-
- Wang Xinmin
- Institute for Materials Research, Tohoku University
-
- Qin Fengxiang
- Institute for Materials Research, Tohoku University
-
- Abe Katsuhiro
- Institute for Materials Research, Tohoku University
-
- Kimura Hisamichi
- Institute for Materials Research, Tohoku University
-
- Inoue Akihisa
- Institute for Materials Research, Tohoku University
書誌事項
- タイトル別名
-
- Temperature-Time-Transformation Curve and Viscous Flow Deformation of Zr<SUB>55</SUB>Cu<SUB>30</SUB>Al<SUB>10</SUB>Ni<SUB>5</SUB> Bulk Glassy Alloy
この論文をさがす
抄録
The temperature-time-transformation curve of a Zr55Cu30Al10Ni5 bulk glassy alloy was obtained by isothermal DSC measurements. High temperature compression tests were carried out to investigate the viscous flow behavior of the Zr55Cu30Al10Ni5 bulk glassy alloy. The influence of four process parameters (temperature, time, initial stress, strain rate) on viscous flow deformation of the bulk glassy alloy was studied. X-ray diffractometry (XRD) was used to examine a glassy state of the glassy alloy samples subjected to viscous flow deformation. Appropriate parameters of viscous flow leading to a good deformation process were proposed. The relative displacement over 80% was obtained by compressing for 200 s at 723 K under a pressure of 160 MPa with a strain rate of 1.32×10−2 s−1. The XRD results showed the absence of crystal peaks after viscous flow deformation under the condition being suggested.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 47 (9), 2308-2311, 2006
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679227611392
-
- NII論文ID
- 130004453306
- 10018249101
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD28XhtFOkur7N
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 8061996
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可