Influences of Potential and pH on Initiation of Environment-Assisted Cracking of Ti-6Al-4V

この論文にアクセスする

この論文をさがす

著者

抄録

We have investigated the influences of potential and pH on environment-assisted cracking (EAC) of Ti–6Al–4V in aqueous solutions. The EAC test was conducted by slow strain rate technique. Solution pH was controlled from 1 to 7, and applied potential was fixed between −1.8 and +0.2 V<SUB>SHE</SUB>. In the solutions of pHs 3 and 7, mechanical properties of the material was almost independent of applied potential. This means that the material shows almost no EAC susceptibility in the potential-pH region for the EAC test period. At pH 1, however, both maximum stress and fracture strain changed with applied potential, and showed minimum values at an applied potential of about −1.0 V<SUB>SHE</SUB>. According to surface analyses by scanning electron microscopy and X-ray diffraction technique, some cracks and Ti hydride were detected from only the specimens fractured at about −1.0 V<SUB>SHE</SUB> in the solution of pH 1. Therefore, it can be concluded that Ti–6Al–4V is most susceptible to the EAC at about −1.0 V<SUB>SHE</SUB> and a pH less than 1. The EAC region was in good agreement with Ti ion stable region in a potential-pH diagram of Ti/water system, and was quite similar to that on the EAC of TiAl.

収録刊行物

  • Materials transactions

    Materials transactions 46(10), 2190-2196, 2005-10-01

    公益社団法人 日本金属学会

参考文献:  23件中 1-23件 を表示

  • <no title>

    KOTFILA R. J.

    Metal Process 66, 128-131, 1954

    被引用文献1件

  • <no title>

    LENNING G. A.

    J. Metals 6, 367-376, 1954

    被引用文献1件

  • <no title>

    BURTE H. M.

    Metals Progress 67, 115-120, 1955

    被引用文献1件

  • <no title>

    NOZUE A.

    Zairyo-to-Kankyo (or Corros. Eng.) 41, 728-733, 1992

    被引用文献1件

  • <no title>

    NOZUE A.

    Zairyo-to-Kankyo (or Corros. Eng.) 44, 287-292, 1995

    被引用文献1件

  • <no title>

    KUMINICK A. J.

    Metall. Trans. 5, 1199-1206, 1974

    被引用文献1件

  • <no title>

    HARUNA T.

    Proc. of 15th Inter. Corros. Cong., 2002, 2002

    被引用文献1件

  • <no title>

    SHIBATA T.

    Zairyo-to-Kankyo (or Corros. Eng.) 41, 217-223, 1992

    被引用文献1件

  • <no title>

    POURBAIX M.

    Atlas of Electrochemical Equilibria in Aqueous Solutions, 1966

    被引用文献1件

  • <no title>

    POURBAIX M.

    Rapports Techniques CEBELCOR 107, RT.146, 1968

    被引用文献1件

  • <no title>

    POURBAIX M.

    The Theory of Stress Corrosion Cracking in Alloys, 1971

    被引用文献1件

  • <no title>

    POURBAIX A.

    Stress Corrosion Mechanisms in Titanium Alloys, 1971

    被引用文献1件

  • <no title>

    WILLIAMS D. N.

    J. Inst. Met. 91, 147-152, 1963

    被引用文献1件

  • <no title>

    SITTING S.

    J. Mater. Sci. : Mater. Med. 10, 35-46, 1999

    被引用文献1件

  • <no title>

    MOODY N. R.

    Meter. Trans., A 11, 973-981, 1980

    被引用文献1件

  • <no title>

    MOODY N. R.

    Meter. Trans., A 13, 1055-1061, 1982

    被引用文献2件

  • <no title>

    HARDIE D.

    Corros. Sci. 41, 155-177, 1999

    被引用文献2件

  • <no title>

    TAKASUGI T.

    Scr. Metall. 19, 903-907, 1985

    被引用文献1件

  • <no title>

    TAKASUGI T.

    J. Mater. Res 7, 2739-2746, 1992

    被引用文献3件

  • Potential-pH region for environment-assisted cracking of gamma titanium aluminide

    HARUNA T.

    Intermetallics 8, 929-935, 2000

    被引用文献3件

  • <no title>

    SCHUTZ R. W.

    Corrosion 37, 585-591, 1981

    被引用文献1件

  • <no title>

    SANDERSON G.

    Corros. Sci. 6, 541-542, 1966

    DOI 被引用文献1件

  • <no title>

    CHANG E.

    Biomater 23, 2917-2925, 2002

    被引用文献1件

被引用文献:  3件中 1-3件 を表示

各種コード

  • NII論文ID(NAID)
    10018277607
  • NII書誌ID(NCID)
    AA1151294X
  • 本文言語コード
    ENG
  • 資料種別
    ART
  • ISSN
    13459678
  • NDL 記事登録ID
    7487810
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z53-J286
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ