Ca, Si含有量に基づく溶融飛灰からのPb, Zn回収方法選択に関する研究 Selection of Cost-effective Zn and Pb Recovery Method from Melting Fly Ash Based on Ca and Si Contents

この論文にアクセスする

この論文をさがす

著者

    • 岡田 敬志 OKADA Takashi
    • 北海道大学大学院工学研究科 環境循環システム専攻廃棄物処分工学研究室 Research Group of Solid Waste Resources Engineering Division of Solid Waste, Resources and Geoenvironmental Engineering Hokkaido University
    • 松藤 敏彦 MATSUTO Toshihiko
    • 北海道大学大学院工学研究科 環境循環システム専攻廃棄物処分工学研究室 Research Group of Solid Waste Resources Engineering Division of Solid Waste, Resources and Geoenvironmental Engineering Hokkaido University
    • 東條 安匡 TOJO Yasumasa
    • 北海道大学大学院工学研究科 環境循環システム専攻廃棄物処分工学研究室 Research Group of Solid Waste Resources Engineering Division of Solid Waste, Resources and Geoenvironmental Engineering Hokkaido University

抄録

溶融飛灰 (以下「飛灰」という) はPb, Zn濃度が高いため, 山元還元による資源としての価値が高い。有用資源の濃縮, 精錬阻害物質除去の前処理が必要であるが, 炉形式, 被溶融物の種類, 消石灰吹き込みの有無などによって溶融飛灰の性状は異なる。そこで本研究では灰溶融19施設, ガス化溶融4施設より溶融飛灰を採取し, 水洗処理, 化学抽出法を行い, 飛灰性状ごとに適用すべき前処理法を検討した。<br>難水溶性物質の主成分はCaとSiであり, Si含有量の高い (おおよそ5%以上) 溶融飛灰はCa濃度によらずPb, Znの抽出が困難であった。Ca含有量の高い (おおよそ10%以上) 溶融飛灰は化学抽出が必要である。CaおよびSi含有量の低い (おおよそ2%以下) 溶融飛灰は水洗処理によってPb, Znを濃縮でき, Pb, Znの含有量が数%と低い場合には低濃度のアルカリあるいは酸による簡易的な化学抽出が適用できる。いずれも, 精錬原料として十分な品位が得られた。Caは消石灰吹き込み, Siはバグフィルタろ布のコーティング剤, 焼却飛灰の混合が, 高含有量の要因である。また, ガス化溶融施設, コークスベッド式灰溶融施設の溶融飛灰はSi含有量が高い。

Fly ash generated from MSW ash-melting and gasification-melting plants, known as Melting Furnace Fly Ash (MFA), is a valuable resource due to its high content of Pb (Lead) and Zn (Zinc) in MFA. In order to recover metals from MFA, pre-treatment for metal enrichment and removal of unwanted elements is necessary. Meanwhile, the elemental composition of MFA depends on the variation of furnace type, input waste, the injection of calcium hydroxide for gas treatment, etc. This study aims to find the most cost-effective recovery method according to the elemental composition of MFA, based on a metal recovery experiment using water washing and several chemical leaching methods applied to MFA samples from nineteen ash melting facilities and four gasification-melting facilities.<br>Ca (Calcium) and Si (Silicon) are the main components of insoluble materials in MFA. When Si content was high, extraction of both Pb and Zn was difficult regardless of Ca content. While chemical leaching was necessary if the MFA contains Ca simple water washing was efficient enough for the MFA when both Si and Ca are in low amounts, although simplified chemical leaching by use of low concentration acid or alkali was necessary when Pb and Zn contents are low. The content of the recovered Pb and Zn met the acceptable quality standard for a smelting furnace. High Ca content was due to the injection of calcium hydroxide and high Si content was due to mixing Si agent for coating the fabric of the bag filter and incineration fly ash with MFA. In addition, Si content was high in MFA generated from the gasification-melting facilities and coke bed ash-melting facility.

収録刊行物

  • 廃棄物学会論文誌 = Journal of the Japan Society Waste Management Experts  

    廃棄物学会論文誌 = Journal of the Japan Society Waste Management Experts 18(1), 8-19, 2007-01-31 

    Japan Society of Material Cycles and Waste Management

参考文献:  19件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  2件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10018291887
  • NII書誌ID(NCID)
    AN10414685
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    1883-1648
  • NDL 記事登録ID
    8652786
  • NDL 雑誌分類
    ZN5(科学技術--建設工学・建設業--都市工学・衛生工学)
  • NDL 請求記号
    Z16-2213
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ