IBAD/MPMT-PLD法による高I_c長尺GdBCO線材の開発 Development of High I_c and Long GdBCO Coated Conductors using IBAD/MPMT-PLD Method

この論文にアクセスする

この論文をさがす

著者

    • 衣斐 顕 IBI Akira
    • 超電導工学研究所 名古屋高温超電導線材開発センター SRL-ISTEC Nagoya Coated Conductor Center
    • 宮田 成紀 MIYATA Seiki
    • 超電導工学研究所 名古屋高温超電導線材開発センター SRL-ISTEC Nagoya Coated Conductor Center

抄録

We have developed high critical current, <i>I</i><sub>c</sub>, and long GdBa<sub>2</sub>Cu<sub>3</sub>O<sub>7-X</sub> (GdBCO) coated conductors using ion-beam assisted deposition (IBAD) / multi-plume and multi-turn pulsed laser deposition (MPMT-PLD) method. We have successfully fabricated 32 and 60.7 m long GdBCO coated conductors with high <i>I</i><sub>c</sub> of 205 and 183 A at 77 K and 0 T, respectively. Moreover, the <i>I</i><sub>c</sub> of the 32 m long GdBCO coated conductor exceeded 20 A at all angles for the applied magnetic field of 3 T. This <i>I</i><sub>c</sub> value at 3 T was 2.5 times higher than that of the 200 A class YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7-X</sub>(YBCO) coated conductor. The production rate of the GdBCO layer was 7.5 to 10 m/h, which is about 2.6 times faster than that for a YBCO layer using the MPMT-PLD method and 10 times faster than that for a YBCO layer using the conventional PLD, single-plume and single-turn PLD, method. In addition, the material yield of the GdBCO layers using the MPMT-PLD method was about 26 to 28%. The GdBCO coated conductors with a high <i>I</i><sub>c</sub> in the magnetic field at 77 K, and capable of being produced quickly and with a high material yield are promising for practical applications.

収録刊行物

  • 低温工学 = Journal of the Cryogenic Society of Japan  

    低温工学 = Journal of the Cryogenic Society of Japan 42(2), 42-46, 2007-02-25 

    CRYOGENICS AND SUPERCONDUCTIVITY SOCIETY OF JAPAN

参考文献:  18件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  1件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

キーワード

各種コード

  • NII論文ID(NAID)
    10018292908
  • NII書誌ID(NCID)
    AN00333419
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    03892441
  • NDL 記事登録ID
    8717276
  • NDL 雑誌分類
    ZM35(科学技術--物理学)
  • NDL 請求記号
    Z15-388
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ