Oxidation or Nitridation Behavior of Pure Chromium and Chromium Alloys Containing 10 mass%Ni or Fe in Atmospheric Heating
-
- Taneichi Kaori
- Department of Materials Processing, Tohoku University
-
- Narushima Takayuki
- Tohoku University Biomedical Engineering Research Organization (TUBERO)
-
- Iguchi Yasutaka
- Department of Materials Processing, Tohoku University
-
- Ouchi Chiaki
- Department of Materials Processing, Tohoku University
書誌事項
- タイトル別名
-
- Oxidation or Nitridation Behavior of Pure Chromium and Chromium Alloys Containing 10massパーセントNi or Fe in Atmospheric Heating
この論文をさがす
抄録
The oxidation or nitridation behavior of pure chromium and chromium alloys containing 10 mass%Ni or 10 mass%Fe in atmospheric heating was investigated in the temperature range of 1073 to 1373 K. The formation behavior of the outer oxide phase of Cr2O3 and its growth kinetics in both chromium alloys was very similar to that of pure chromium. The nitride layer with the Cr2N phase was formed beneath the oxide phase at temperatures above 1273 K in pure chromium. Marked internal nitridation with the formation of the Cr2N phase was observed in the Cr-10 mass%Fe alloy, while the formation of Cr2N was negligible in the Cr-10 mass%Ni alloy. Neither Ni nor Fe were detected inside the Cr2O3 phase, and was enriched in the subsurface layer between the oxide layer and the base alloy in a respective alloy. The Ni-enriched layer in Cr-10 mass%Ni alloy had a relatively narrow width, but a very high concentration of Ni compared with the Fe-enriched layer formed in the Cr-10 mass%Fe alloy.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 47 (10), 2540-2546, 2006
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679227380480
-
- NII論文ID
- 10018310353
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- HANDLE
- 10097/00127747
-
- NDL書誌ID
- 8092125
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- IRDB
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可